Failure Analysis of Disbondment of Three-Layer Polyethylene Coatings from the Surface of Buried Steel Pipelines

详细信息    查看全文

• 作者：Mansour Rahsepar ; Mohammad Asgharzadeh…
• 关键词：Coating ; Failure analysis ; Three ; layer polyethylene ; Disbondment
• 刊名：Journal of Failure Analysis and Prevention
• 出版年：2015
• 出版时间：October 2015
• 年：2015
• 卷：15
• 期：5
• 页码：604-611
• 全文大小：1,174 KB
• 参考文献：1.J.M. Pommersheim, T. Nguyen, Degradation of organic coatings on steel: mathematical models and predictions. Prog. Org. Coat. 25, 23鈥?1 (1994)CrossRef
  2.G. Grundmeier, W. Schmidt, M. Stratmann, Corrosion protection by organic coatings: electrochemical mechanism and novel methods of investigation. Electrochim. Acta 45, 2515鈥?533 (2000)CrossRef
  3.M.I. Karyakina, A.E. Kuzmak, Protection by organic coatings: criteria, testing methods and modelling. Prog. Org. Coat. 18, 325鈥?88 (1990)CrossRef
  4.G.P. Guidetti, G.L. Rigosi, R. Marzola, The use of polypropylene in pipeline coatings. Prog. Org. Coat. 27, 79鈥?5 (1996)CrossRef
  5.G.R. Howell, Y.F. Cheng, Characterization of high performance composite coating for the northern pipeline application. Prog. Org. Coat. 60, 148鈥?52 (2007)CrossRef
  6.Y. Joliff, L. Belec, E. Aragon, Influence of the thickness of pipeline coating on internal stresses during the manufacturing process by finite element analysis. Comput. Mater. Sci. 68, 342鈥?49 (2013)CrossRef
  7.E. Legghe, Y. Joliff, L. Belec, L. Aragon, A. Margaillan, Computational analysis of internal stresses generated during the manufacturing process of a monolayer or three-layer pipeline coating. Comput. Mater. Sci. 48, 360鈥?65 (2010)CrossRef
  8.E. Legghe, Y. Joliff, L. Belec, E. Aragon, Computational analysis of a three-layer pipeline coating: internal stresses generated during the manufacturing process. Comput. Mater. Sci. 50, 1533鈥?542 (2011)CrossRef
  9.D. Melot, G. Paugam, M. Roche, Disbondments of Pipelines Coatings and Their Consequences on Corrosion Risks, 17th International Conference on Pipeline Protection, BHR Group, Edinburgh, 2007.
  10.M. Roche, An Experience in Offshore Pipeline Coatings, Corrosion, 2004鈥擭ACE International, New Orleans, USA, 2004.
  11.M. Roche, D. Melot, G. Paugam, Recent Experience with Pipeline Coating Failures, 16th International Conference on Pipeline Protection, BHR Group, Paphos, Cyprus, 2005.
  12.M. Roche, External Coatings of Pipelines: Challenges Related to Corrosion Risks, Iranian Corrosion/2007鈥擨CA International Congress, Tehran, 2007.
  13.C. Argent, D. Norman, Three Layer Polyolefin Coatings: Fulfilling Their Potential? Corrosion 2006, 12鈥?6 March, San Diego, California, USA, 2006
  14.C. Argent, D. Norman, Fitness for Purpose Issues Relating to FBE and Three Layer PE Coatings, Corrosion 2005, 3鈥? April, Houston, Texas, USA, 2005
  15.H. Leidheiser, W. Wang, L. Igetoft, The mechanism for the cathodic delamination of organic coatings from a metal surface. Prog. Org. Coat. 11, 19鈥?0 (1983)CrossRef
  16.D. Roy, G.R. Simon, M. Forsyth, J. Marde, Modification of thermoplastic coatings for improved cathodic disbondment performance on a steel substrate: a study on failure mechanisms. Int. J. Adhes. Adhes. 22, 395鈥?03 (2002)CrossRef
  17.F.M. Song, N. Sridhar, Modeling pipeline crevice corrosion under a disbonded coating with or without cathodic protection under transient and steady state conditions. Corros. Sci. 50, 70鈥?3 (2008)CrossRef
  
• 作者单位：Mansour Rahsepar (1)
  Mohammad Asgharzadeh (1)
  Mohammad Jafar Hadianfard (1)
  Seyed Ahmad Jenabali Jahromi (1)
  
  1. Department of Materials Science and Engineering, School of Engineering, Shiraz University, Zand Boulevard, 7134851154, Shiraz, Iran
  
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Chemistry
  Materials Science
  Tribology, Corrosion and Coatings
  Characterization and Evaluation Materials
  Mechanics
  Structural Mechanics
  Quality Control, Reliability, Safety and Risk
  
• 出版者：Springer Boston
• ISSN：1864-1245

文摘

A failure analysis was conducted to analyze the mode and causes of the disbondment of the three-layer polyethylene coatings from the surface of buried steel pipelines. The failure interface was analyzed through visual and microscopy investigations. Analysis of the coating at the disbonded interface revealed that the fusion bonded epoxy (FBE) layer had a fragile integrity which may have resulted from the in-service conditions of the pipeline. According to failure analysis of the disbonded interface, it can be concluded that degradation of the molecular structure of FBE layer was the most probable cause of the coating failure. It is believed that degradation of the molecular structure of FBE layer and subsequent disbondment of the coatings was caused by a mechanical-assisted cathodic delamination process which was due to the simultaneous action of chemical degradation and residual stresses at the coating-substrate interface. It is believed that surface pretreatment of the steel substrate in addition to coating process parameters of the powder coating are the main parameters in determining the long-term performance of the coating-substrate interface and should be carefully controlled. Keywords Coating Failure analysis Three-layer polyethylene Disbondment