Hybrid nanocomposite membranes of sulfonated poly(ethersulfone)/1,1-carbonyl diimidazole/1-(3-aminopropyl)-silane/silica for direct methanol fuel cells

详细信息    查看全文

• 作者：Yasamin Khosravi ; Shadi Hassanajili…
• 关键词：Membrane ; Sulfonated Poly(ethersulfone) ; Silica ; Nafion 117 ; Methanol Permeability ; Proton Conductivity
• 刊名：Korean Journal of Chemical Engineering
• 出版年：2017
• 出版时间：February 2017
• 年：2017
• 卷：34
• 期：2
• 页码：328-339
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Industrial Chemistry/Chemical Engineering; Catalysis; Materials Science, general; Biotechnology;
• 出版者：Springer US
• ISSN：1975-7220
• 卷排序：34

文摘

Composite membranes of sulfonated poly(ethersulfone)/1,1-carbonyl diimidazole/1-(3-aminopropyl)-silane/silica (SPES/CDI/AS/SiO₂) with silica of various contents (3, 5 and 8 wt%) were prepared as electrolytes for direct methanol fuel cells (DMFCs). Comparison was made with pure SPES and SPES/SiO₂. The properties of the composite membranes were studied by FTIR, TGA, XRD, water and methanol uptake, proton conductivity. SPES/CDI/AS/SiO₂ membranes were also characterized by scanning electron microscopy (SEM), which showed good adhesion between the modified sulfonic acid (-SO3H) groups of SPES and silica because of cross-linking with covalent bond formation and reduced cavities in the composites. This effect played an important role in reducing water uptake, methanol uptake and methanol permeability of the SPES/CDI/AS/SiO₂ composites. The water and methanol uptake and also methanol permeability of the SPES/CDI/AS/SiO₂ composite membrane with 8% SiO₂ were found in the order 3.58%, 2.48% and 1.91×10−7 (cm2s−1), lower than those of SPES and Nafion 117. In SPES membrane of 16.94% level of sulfonation, the proton conductivity was 0.0135 s/cm at 25 °C, which approached that of Nafion 117 under the same conditions. Also, the proton conductivity of the SPES/CDI/AS/SiO₂ 8% membrane was 0.0186 s/cm, which was higher than that of SPES at room temperature. The preparation of SPES/SiO₂ composites in the presence of AS and CDI, led to 63%, 56% and 64% reduction of water uptake, methanol uptake and methanol permeability, respectively without a sharp drop in proton conductivity of the composite membranes which featured a good balance between high proton conductivity, water and methanol uptake of SPES/CDI/AS/SiO₂ membranes.