A Comparative Study on the Hot Working Behavior of Inconel 718 and ALLVAC 718 Plus

详细信息    查看全文

• 作者：Amir Momeni ; Seyed Mehdi Abbasi…
• 刊名：Metallurgical and Materials Transactions A
• 出版年：2017
• 出版时间：March 2017
• 年：2017
• 卷：48
• 期：3
• 页码：1216-1229
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Metallic Materials; Characterization and Evaluation of Materials; Structural Materials; Surfaces and Interfaces, Thin Films; Nanotechnology;
• 出版者：Springer US
• ISSN：1543-1940
• 卷排序：48

文摘

Hot compression tests were performed on Inconel 718 and ALLVAC 718 PLUS (718+) at temperatures and strain rates in ranges of 1223 K to 1373 K (950 °C to 1100 °C) and 0.001–1 s−1, respectively. Discontinuous yield behavior was observed in the flow curves of both alloys. For both alloys, the drop in stress at the yield point (yield drop) was maximized at 0.01 to 1 s−1. The alloy 718+ showed larger yield drop than 718 over the studied deformation conditions. The different yield behaviors were attributed to the various chemical compositions. The peak strain for both alloys increased in temperature range of 1223 K to 1273 K (950 to 1000 °C) and strain rates of 0.01 to 1 s−1. This uncommon behavior was ascribed to the change in the mechanism of microstructural evolution from continuous to discontinuous dynamic recrystallization (DRX). The kinetics of DRX was described by the Avrami equation and the exponent was determined at different deformation conditions. The Avrami exponent increased in the middle values of Zener–Hollomon (Z) parameters, i.e., 29.3 < lnZ < 32.9 for 718 and 31.4 < lnZ < 34.5 for 718+. The unusual variation of the Avrami exponent was attributed to the change in the mechanism of DRX.