Effect of triblock copolymers on homogeneity, mechanical properties and swelling behavior of IIR/SBR rubber blends

详细信息    查看全文

• 作者：M. M. Eissa ; S. H. Botros ; A. F. Moustafa
• 关键词：Triblock copolymers ; Butyl rubber ; SBR ; Rubber blends ; Physico ; mechanical properties ; Homogeneity
• 刊名：Polymer Bulletin
• 出版年：2017
• 出版时间：February 2017
• 年：2017
• 卷：74
• 期：2
• 页码：393-412
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Polymer Sciences; Soft and Granular Matter, Complex Fluids and Microfluidics; Characterization and Evaluation of Materials; Physical Chemistry;
• 出版者：Springer Berlin Heidelberg
• ISSN：1436-2449
• 卷排序：74

文摘

The present research concerns with the preparation and characterization of isobutylene isoprene/butadiene–styrene rubber (IIR/SBR) blends with different blend ratios, in the presence and absence of styrene–isoprene–styrene (SIS) and styrene–isobutylene–styrene (SiBS) triblock copolymers to be tested as compatibilizers. Effect of the triblock copolymers on the blend homogeneity was investigated with the aid of scanning electron microscopy (SEM) and differential scanning calorimetry (DSC) measurements. Characterization of the rubber blends was conducted by measuring the physico-mechanical properties after and before thermal aging, in presence and absence of the triblock copolymers. In addition, weight swell % in toluene, motor oil and brake fluid of the rubber blend vulcanizates was assessed. The incorporation of SIS and SiBS triblock copolymers improved the homogeneity of IIR/SBR blends as well as increased both tensile strength and elongation at break of the rubber blend vulcanizates. Of the entire blend ratios examined, IIR/SBR (25/75) blend containing SIS compatibilizer possessed the best physico-mechanical properties (12.6 MPa tensile strength and 425 % elongation at break) and (14 MPa tensile strength and 555 % elongation at break) after and before thermal aging, respectively. Utilization of SIS and SiBS triblock copolymers enhanced the thermal stability of IIR/SBR blend vulcanizates. Moreover, IIR/SBR blends of different blend ratios showed superior swelling resistance in the brake fluid. IIR/SBR (25/75) blend containing SIS compatibilizer and cured with CBS/ZDEC/S vulcanizing system possessed the best physico-mechanical properties (14.4 MPa tensile strength and 440 % elongation at break) and (16.5 MPa tensile strength and 610 % elongation at break) after and before thermal aging, respectively.