Effect of work hardening of cobalt in sintered carbide cutting tool on tool failure during interrupted cutting

详细信息    查看全文

• 作者：Erhan Altan ; Alper Uysal ; Şeref Han Anaç…
• 关键词：Interrupted cutting ; Work hardening of cobalt ; Carbide tool ; Fatigue
• 刊名：The International Journal of Advanced Manufacturing Technology
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：88
• 期：1-4
• 页码：359-367
• 全文大小：
• 刊物类别：Engineering
• 刊物主题：Industrial and Production Engineering; Media Management; Mechanical Engineering; Computer-Aided Engineering (CAD, CAE) and Design;
• 出版者：Springer London
• ISSN：1433-3015
• 卷排序：88

文摘

In interrupted cutting, chips occur as intermittent and cutting tool may be damaged under severe variable loading. And it is known that the cutting forces cause transverse cracks on the rake face, and cutting tool may be damaged during interrupted cutting under mechanical and thermal fatigue in a short period of time. In this work, carbide inserts and forged SAE 4340 workpiece with axial slots were used in interrupted turning. The hardness values of some points on rake face near the cutting edge were measured, and cracks and failures on cutting tool were displayed by scanning electron microscopy (SEM). Additionally, milling experiments were conducted with carbide inserts on C45 medium carbon steel. In the interrupted cutting, the effect of work hardening of cobalt in sintered carbide cutting tool on tool failure was investigated. According to the results, micro hardness of sintered carbide cutting tool increased due to work hardening of cobalt, and this caused the micro crack formation on cutting tool.