Microstructures and properties of Al2O3 dispersion-strengthened copper alloys prepared through different methods
详细信息    查看全文
  • 作者:Zhi-qiao Yan ; Feng Chen ; Fu-xing Ye
  • 关键词:dispersion ; strengthened alloys ; copper alloys ; alumina ; preparation methods ; microstructure ; properties
  • 刊名:International Journal of Minerals, Metallurgy, and Materials
  • 出版年:2016
  • 出版时间:December 2016
  • 年:2016
  • 卷:23
  • 期:12
  • 页码:1437-1443
  • 全文大小:
  • 刊物类别:Chemistry and Materials Science
  • 刊物主题:Materials Science, general; Metallic Materials; Characterization and Evaluation of Materials; Ceramics, Glass, Composites, Natural Materials; Surfaces and Interfaces, Thin Films; Tribology, Corrosion
  • 出版者:University of Science and Technology Beijing
  • ISSN:1869-103X
  • 卷排序:23
文摘
Al2O3 dispersion copper alloy powder was prepared by internal oxidation, and three consolidation methods—high-velocity compaction (HVC), hot pressing (HP), and hot extrusion (HE)—were used to prepare Al2O3 dispersion-strengthened copper (Cu–Al2O3) alloys. The microstructures and properties of these alloys were investigated and compared. The results show that the alloys prepared by the HP and HE methods exhibited the coarsest and finest grain sizes, respectively. The alloy prepared by the HVC method exhibited the lowest relative density (98.3% vs. 99.5% for HP and 100% for HE), which resulted in the lowest electrical conductivity (81% IACS vs. 86% IACS for HP and 87% IACS for HE). However, this alloy also exhibited the highest hardness (77 HRB vs. 69 HRB for HP and 70 HRB for HE), the highest compressive strength (443 MPa vs. 386 MPa for HP and 378 MPa for HE), and the best hardness retention among the investigated alloys. The results illustrate that the alloy prepared by the HVC method exhibits high softening temperature and good mechanical properties at high temperatures, which imply long service life when used as spot-welding electrodes.