文摘
Thermal behaviour of cure-accelerated phenol-formaldehyde (PF) resins was studied using the addition of commercial mixture of water soluble oil shale alkylresorcinols (AR) to PF resin, 5-MR being as model compound. The acceleration effect of AR is based on the promotion of condensation of resin methylol groups and subsequent reaction of released formaldehyde with AR. Commercial PF resins SFŽ-3013VL and SFŽ-3014 from the Estonian factory VKG Resins have been used. The chemical structure of resins was characterised by 13C NMR spectroscopy. TG-DTA analysis was carried out using labsysTM instrument Setaram. By TG-DTA measurements, the shift of exothermic and endothermic peaks and the changes of mass loss rate in the ranges of 1.5–10 g AR/100 g PF resin were studied. The effect of AR on the curing behaviour of PF resins was also followed by gel time. Testing of the plywood when using PF resin with 5 mass% of AR shows that the press time could be reduced by about 15%.