文摘
The texture development during friction stir processing (FSP) of 1050 aluminum severely deformed at the strain magnitude of 2.32 was comprehensively discussed. It was observed that the component \( \bar{B} \) of the ideal shear texture along with the cube texture was developed in the severely deformed base metal. The effects of base metal texture on the texture development of stir zone, thermo-mechanically affected zone, and heat-affected zone during FSP were examined. Also, the developed texture components in the vicinity of the FSP tool and the stir zone were correlated to the deformation induced by the rotating tool which consisted of pin and shoulder. The observed texture components in the longitudinal section of the stir zone were found coincided with the ideal shear ones, but different from those observed in the severely deformed base metal. It could be responsible for the fact that the material beneath the FSP tool is predominantly deformed and stirred by the shoulder rather than the pin. The independency of texture development in the stir zone from pin-induced deformation was also consistent with the observation associated with the stir zone geometry which was independent of the pin geometry. Microstructural evolutions in the regions located ahead of the FSP tool manifested the incident of static recovery and recrystallization as a result of the stored strain in the severely deformed base metal. These led to the development of almost random texture and the deterioration of base metal texture in this region. This suggested the independency of texture development in the stir zone from the texture of severely deformed base metal.