参考文献:1. S.R. Bakshi, D. Lahiri, A. Agarwal, Int. Mater. Rev. 55, 41 (2010) CrossRef 2. J.C. Lee, J.P. Ahn, J.H. Shim, Z. Shi, H.I. Lee, Scr. Mater. 41, 895 (1999) CrossRef 3. S. Warrier, C. Blue, R. Lin, J. Mater. Sci. 28, 760 (1993) CrossRef 4. S.R. Bakshi, V. Singh, S. Seal, A. Agarwal, Surf. Coat. Technol. 203, 1544 (2009) CrossRef 5. S. Salimi, H. Izadi, A. Gerlich, J. Mater. Sci. 46, 409 (2011) CrossRef 6. Q. Li, C.A. Rottmair, R.F. Singer, Compos. Sci. Technol. 70, 2242 (2010) CrossRef 7. B. Abbasipour, B. Niroumand, S.M. Monir Vaghefi, Trans. Nonferrous. Met. Soc. China 20, 1561 (2010) CrossRef 8. H. Uozumi, K. Kobayashi, K. Nakanishi, T. Matsunaga, K. Shinozaki, H. Sakamoto, T. Tsukada, C. Masuda, M. Yoshida, Mater. Sci. Eng. A 495, 282 (2008) CrossRef 9. K. Morsi, A. Esawi, J. Mater. Sci. 42, 4954 (2007) CrossRef 10. A.M.K. Esawi, K. Morsi, A. Sayed, A.A. Gawad, P. Borah, Mater. Sci. Eng. A 508, 167 (2009) CrossRef 11. D. Poirier, R. Gauvin, R.A.L. Drew, Compos. A 40, 1482 (2009) CrossRef 12. L. Jiang, Z. Li, G. Fan, L. Cao, D. Zhang, Carbon 50, 1993 (2012) CrossRef 13. C. He, N. Zhao, C. Shi, X. Du, J. Li, H. Li, Q. Cui, Adv. Mater. 19, 1128 (2007) CrossRef 14. X. Yang, E. Liu, C. Shi, C. He, J. Li, N. Zhao, K. Kondoh, J. Alloys Compd. 563, 216 (2013) CrossRef 15. H. Wei, Z. Li, D.B. Xiong, Z. Tan, G. Fan, Z. Qin, D. Zhang, Scr. Mater. 75, 30 (2014) CrossRef 16. A.M.K. Esawi, M.A. El Borady, Compos. Sci. Technol. 68, 486 (2008) CrossRef 17. C. Deng, D. Wang, X. Zhang, A. Li, Mater. Sci. Eng. A 444, 138 (2007) CrossRef 18. T. Kuzumaki, K. Miyazawa, H. Ichinose, K. Ito, J. Mater. Res. 13, 2445 (1998) CrossRef 19. L. Ci, Z. Ryu, N.Y. Jin-Phillipp, M. Rühle, Acta Mater. 54, 5367 (2006) CrossRef 20. H. Kwon, M. Estili, K. Takagi, T. Miyazaki, A. Kawasaki, Carbon 47,
作者单位:Genlian Fan (1) Ziyun Yu (1) Zhanqiu Tan (1) Zhiqiang Li (1) Di Zhang (1)
1. State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai, 200240, China
ISSN:2194-1289
文摘
This review summarizes the work carried out in the field of interface study in carbon nanotube reinforced aluminum (CNT/Al) composites. Much research work has been conducted to reveal the evolution of CNT/Al interface in producing the composite with the purpose of achieving uniform distribution of CNTs and tight interfacial bonding. The effect and principles of coating were reviewed along with the illustration of “intermetallic interphases-design. Different roles of CNT/Al interface in structural and functional application were elucidated, and the future work that needs attention was addressed.