Network-forming As2(S/Se)m nanoclusters are employed to recognize expected variations in a vicinity of some remarkable compositions in binary As–Se/S glassy systems accepted as signatures of optimally constrained intermediate topological phases in earlier temperature-modulated differential scanning calorimetry experiments. The ab initio quantum chemical calculations performed using the cation-interlinking network cluster approach show similar oscillating character in tendency to local chemical decomposition but obvious step-like behavior in preference to global phase separation on boundary chemical compounds (pure chalcogen and stoichiometric arsenic chalcogenides). The onsets of stability are defined for chalcogen-rich glasses, these being connected with As2Se5 (Z = 2.29) and As2S6 (Z = 2.25) nanoclusters for As–Se and As–S glasses, respectively. The physical aging effects result preferentially from global phase separation in As–S glass system due to high localization of covalent bonding and local demixing on neighboring As2Sem+1 and As2Sem−1 nanoclusters in As–Se system. These nanoclusters well explain the lower limits of reversibility windows in temperature-modulated differential scanning calorimetry, but they cannot be accepted as signatures of topological phase transitions in respect to the rigidity theory.