参考文献:[1]H. Ahn, J-H. Park, S-B. Kim, S. H. Jee, Y. S. Yoon and D-J. Kim, Electrochem. Solid-State Lett. 13, J125 (2010). [2]I. Corni, M. P. Ryan and A. R. Boccaccini, J. Eur. Ceram. Soc. 28, 1353 (2008).View Article [3]Y. C. Wang, I. C. Leu and M. H. Hon, J. Am. Ceram. Soc. 87, 84 (2004).View Article [4]L. Besra, C. Compson and M. Liu, J. Am. Ceram. Soc. 89, 3003 (2006).View Article [5]L. Besra and M. Liu, Prog. Mater Sci. 52, 1 (2007).View Article [6]A. R. Boccaccini, J. Cho, J. A. Roether, B. J. C. Thomas, E. J. Minay and M. S. P. Shaffer, Carbon 44, 3149 (2006).View Article [7]S. Park and S. Jayaraman, MRS Bull. 28, 585 (2003).View Article [8]J. Bae, M. K. Song, Y. J. Park, J. M. Kim, M. Liu and Z. L. Wang, Angew. Chem. Int. Ed. 50, 1683 (2011).View Article [9]H. Park et al., Mater. Lett. 118, 47 (2014).View Article [10]F. Tang, T. Uchikoshi and Y. Sakka, J. Am. Ceram. Soc. 85, 2161 (2002).View Article [11]M. Verde, M. Peiteado, A. C. Caballero, M. Villegas and B. Ferrari, J. Colloid. Interf. Sci. 373, 27 (2012).View Article [12]Y. Chung, H. Park, S. B. Cho, Y. S. Yoon and D-J. Kim, J. Ceram. Process. Res. 15, 331 (2014). [13]H. C. Hamaker, Trans. Faraday Soc. 35, 279 (1940).View Article [14]N. Sato, M. Kawachi, K. Noto, N. Yoshimoto and M. Yoshizawa, Physica C 357鈥?60, 1019 (2001).View Article [15]H. Farnoush, J. A. Mohandesi and D. H. Fatmehsari, Int. J. Appl. Ceram. Technol. 10, 87 (2013).View Article [16]A. R. Boccaccini, U. Schindler and H. G. Kr篓uger, Mater. Lett. 51, 225 (2001).View Article [17]S. Wang and R. A. W. Dryfe, J. Mater. Chem. A. 1, 5279 (2013).View Article [18]Z. Fan and J. G. Lu, J. Nanosci. Nanotechnol. 5, 1561 (2005).View Article [19]Y. C. Wang, I. C. Leu and M. H. Hon, J. Appl. Phys. 95, 1444 (2004).View Article ADS [20]Y. Yang, W. Guo, X. Wang, Z. Wang, J. Qi and Y. Zhang, Nano Lett. 12, 1919 (2012).View Article ADS [21]S. J. Penn, N. M. Alford, A. Templeton, X. Wang, M. Xu, M. Reece and K. Schrapel, J. Am. Ceram. Soc. 80, 1885 (1997).View Article
作者单位:Yoonsung Chung (1) Hyejin Park (1) Dong-Joo Kim (1) Sung Baek Cho (2) Young Soo Yoon (3)
1. Materials Research and Education Center, Auburn University, Auburn, AL, 36849, USA 2. Advanced Technology Research Center, Agency for Defense Development, Daejeon, 305-600, Korea 3. Department of Chemical Engineering, Gachon University, Seongnam, 461-701, Korea
刊物主题:Physics, general; Theoretical, Mathematical and Computational Physics; Particle and Nuclear Physics;
出版者:Springer Netherlands
ISSN:1976-8524
文摘
The deposition behavior of ZnO nanoparticles on metal plates and conductive fabrics was investigated using electrophoretic deposition (EPD). The deposition kinetics on both metal plates and fabrics were examined using the Hamaker equation. Fabric substrates give more deposited weight than flat substrates due to their rougher shape and higher surface area. The morphologies and the structures of the deposited ZnO layers showed uniform deposition without any preferred orientation on both substrates. The dielectric properties of the ZnO layers formed by using EPD showed values that were reduced, but comparable to those of bulk ZnO. This result suggests that EPD is a convenient method to deposit functional oxides on flexible substrates.