Nanocrystallization of Fe_73.5Si_13.5B₉Nb₃Cu₁ soft-magnetic alloy from amorphous precursor in a magnetic field

详细信息    查看全文

• 作者：Hiromichi Fujii ; Victoria A. Yardley ; Takashi Matsuzaki and Sadahiro Tsurekawa
• 刊名：Journal of Materials Science
• 出版年：2008
• 出版时间：June, 2008
• 年：2008
• 卷：43
• 期：11
• 页码：3837-3847
• 全文大小：613.7 KB

文摘

The effect of a magnetic field on the nature of nanocrystallization from a melt-spun Fe_73.5Si_13.5B₉Nb₃Cu₁ amorphous precursor has been studied with the aim of controlling microstructures and magnetic properties. Annealing for magnetic crystallization was carried out at temperatures between the Curie temperature of the amorphous phase (586 K) and that of the crystalline phase (920 K). It was found that the {110} texture component in crystallized α-Fe(Si) phase increased in importance with increasing magnetic-field strength. An X-ray diffraction analysis based on the Shultz method revealed that the magnetic field caused preferential formation of {110}-oriented nuclei. In addition, the applied field enhanced crystallization kinetics, particularly the nucleation rate. No significant difference in grain growth behavior was observed as a result of applying a magnetic field. We therefore conclude that the development of the {110} texture by magnetic crystallization is predominantly attributable to preferential nucleation, rather than preferential growth, of {110}-oriented nuclei. The saturation magnetization of nanocrystallized specimens, evaluated using a vibrating sample magnetometer (VSM), was increased by the application of a magnetic field up to 4T during nanocrystallization.