参考文献:1.E.J. Hoggan, R.I. Scott, M.R. Barnett, P.D. Hodgson, Mechanical properties of tension leveled and skin passed steels. J. Mater. Process. Technol. 125–126, 155–163 (2002)CrossRef 2. http://www.keytometals.com/page.aspx?ID=CheckArticle&site=kts&NM=392 . Accessed Feb 2013 3.Cold rolled carbon steel flat products for vitreous enameling, Technical Delivery Conditions, British Standard BS EN 10209
作者单位:Ahmed Ismail Zaky Farahat (1) Ahmed M. Bahgat Gemeal (1) Ramadhan N. Elshaer (1)
1. Central Metallurgical R&D Institute, Metals Technology, P.O. Box 87, Helwan, Cairo, Egypt
刊物类别:Chemistry and Materials Science
刊物主题:Chemistry Materials Science Tribology, Corrosion and Coatings Characterization and Evaluation Materials Mechanics Structural Mechanics Quality Control, Reliability, Safety and Risk
出版者:Springer Boston
ISSN:1864-1245
文摘
This paper studies the behavior of non-alloy sheet steel in very low plastic deformation. The steel was subjected to temper rolling (skin pass) with different ratios till 5%. The sheet steel also was subjected to aging after temper rolling. The tensile curves were plotted and their characteristics were determined. The work-hardening coefficient (n) was determined after temper rolling directly and after aging to judge the general behavior of sheets. The microstructure observation was carried out o notice the surface stretcher strains (kinks). Lüder’s bands were observed in aged steel sheets leading to high surface roughness. The surface roughness was measured after temper rolling or aging to judge the surface quality. Keywords Steel sheets Orange peel Lüder’s bands Skin pass Temper rolling Yield strength Surface roughness