刊名:Journal of Inorganic and Organometallic Polymers and Materials
出版年:2013
出版时间:July 2013
年:2013
卷:23
期:4
页码:798-802
全文大小:418KB
参考文献:1. J. Wang, Z.Q. Lin, Chem. Mater. 22, 579 (2010) CrossRef 2. C.J. Lin, W.Y. Yu, S.H. Chien, J. Mater. Chem. 20, 1073 (2010) CrossRef 3. M. Paulose, K. Shankar, S. Yoriya, H.E. Prakasam, O.K. Varghese, G.K. Mor, T. Latempa, A. Fitzgerald, C.A. Grimes, J. Phys. Chem. B 110, 16179 (2006) CrossRef 4. K. Shankar, G.K. Mor, H.E. Prakasam, S. Yoriya, M. Paulose, O.K. Varghese, C.A. Grimes, Nanotechnology 18, 065707 (2007) CrossRef 5. K. Zhu, N.R. Neale, A. Miedaner, A.J. Frank, Nano Lett. 7, 69 (2007) CrossRef 6. J.R. Jennings, A. Ghicov, L.M. Peter, P. Schmuki, A.B. Walker, J. Am. Chem. Soc. 130, 13364 (2008) CrossRef 7. O.K. Varghese, M. Paulose, C.A. Grimes, Nat. Nanotechnol. 4, 592 (2009) CrossRef 8. H. Park, W.R. Kim, H.T. Jeong, J.J. Lee, H.G. Kim, W.Y. Choi, Sol. Energy Mater. Sol. Cells 95, 184 (2011) CrossRef 9. X.F. Guan, S.Q. Huang, Q.X. Zhang, X. Shen, H.C. Sun, D.M. Li, Y.H. Luo, R.C. Yu, Q.B. Meng, Nanotechnology 22, 465402 (2011) CrossRef 10. A. Yella, H.W. Lee, H.N. Tsao, C.Y. Yi, A.K. Chandiran, M.K. Nazeeruddin, E. W-G, C.Y. Diau, S.M. Yeh, M.Gr?tzel Zakeeruddin, Science 334, 629 (2011) CrossRef 11. Y.L. Lee, Y.S. Lo, Adv. Funct. Mater. 19, 604 (2009) CrossRef 12. S.Q. Huang, Q.X. Zhang, X.M. Huang, X.Z. Guo, M.H. Deng, D.M. Li, Y.H. Luo, Q. Shen, T. Toyoda, Q.B. Meng, Nanotechnology 21, 375201 (2010) CrossRef 13. W. Yu, L.H. Qu, W.Z. Guo, X.G. Peng, Chem. Mater. 15, 2854 (2003) CrossRef 14. A. Kongkanand, K. Tvrdy, K. Takechi, M. Kuno, P.V. Kamat, J. Am. Chem. Soc. 130, 4007 (2008) CrossRef 15. J.B. Sambur, T. Novet, B.A. Parkinson, Science 330, 63 (2010) CrossRef 16. M.C. Hanna, A.J. Nozic, J. Appl. Phys. 100, 074510 (2006) CrossRef 17. L. Li, X.C. Yang, J.J. Gao, H.N. Tian, J.Z. Zhao, A. Hagfeldt, L.C. Sun, J. Am. Chem. Soc. 133, 8458 (2011) CrossRef 18. H.J. Lee, M.K. Wang, P. Chen, D.R. Gamelin, S.M. Zakeeruddin, M. Gr?tzel, M.K. Nazeeruddin, Nano Lett. 9, 4221 (2009) CrossRef 19. H.J. Lee, P. Chen, S.J. Moon, F. Sauvage, K. Sivula, T. Bessho, D.R. Gamelin, P. Comte, S.M. Zakeerudin, S. Seok, M. Gr?tze, M.K. Nazeeruddin, Langmuir 25, 7602 (2009) CrossRef 20. A. Zaban, O.I. Micici, B.A. Gregg, A.J. Nozik, Langmuir 14, 3153 (1998) CrossRef 21. G. Larramona, C. Chone, A. Jacob, D. Sakakura, B. Delatouche, D. Pere, X. Cieren, M. Nagino, R. Bayon, Chem. Mater. 18, 1688 (2006) CrossRef 22. X.T. Ma, Y. Shen, G.Z. Wu, Q.S. Wu, B.H. Pei, M. Cao, F. Gu, J Alloy Compd. 538, 61 (2012) CrossRef 23. Y.L. Lee, C.H. Chang, J. Power Sour. 185, 584 (2008) CrossRef 24. N.G. Park, V.D.J. Lagemaat, A.J. Frank, J. Phys. Chem. B 104, 8989 (2000) CrossRef 25. J. Wang, Z.Q. Lin, Chem. Mater. 20, 1257 (2008) CrossRef 26. T. Stergiopoulos, A. Ghicov, V. Likodimos, D.S. Tsoukleris, J. Kunze, P. Schmuki, P. Falaras, Nanotechnology 19, 235602 (2008) CrossRef 27. L. Zeiri, I. Patla, S. Acharya, Y. Golan, S. Efrima, J. Phys. Chem. C 111, 11843 (2007) CrossRef 28. H. Chen, W. Fu, H. Yang, P. Su, Y.Y. Zhang, L.R. Wang, W.Y. Zhao, X.M. Zhou, H. Zhao, Q. Jing, X.F. Qi, Y.X. Li, Electrochim. Acta 56, 919 (2010) CrossRef
作者单位:Xiaotian Ma (1) Yue Shen (1) Qishuang Wu (1) Tan Shen (1) Meng Cao (1) Feng Gu (1) Linjun Wang (1)
1. School of Materials Science and Engineering, Shanghai University, 149 Yan Chang Rd, Shanghai, 200072, People’s Republic of China
ISSN:1574-1451
文摘
Front-side illuminated CdS quantum dots (QDs) sensitized solar cells (QDSSCs) based on TiO2 nanotube arrays (TNTAs) were fabricated. The free-standing TNTAs (f-TNTAs) membranes were obtained from anodic oxidized Ti foils by self-detaching technique and then transferred to FTO glass substrates to form photoanodes. CdS QDs were loaded on TNTAs by sequential chemical bath deposition approach. Scanning electron microscope (SEM) results indicated that the morphology and structure of TNTAs membranes did not change in detaching and transferring process. Power conversion efficiency of the devices from the front-side illumination mode is 1.47?%, which is much higher than that (0.34?%) of the back-side illumination mode owing to the markedly improved light absorption.