Non-isothermal crystallization kinetics and activation energy of bio-based poly(trimethylene terephthalate)/poly(butylene adipate-co-terephthalate) polyester blend
参考文献:1.P. Hong, W. Chung, and C. Hsu, Polymer 43, 3335 (2002).CrossRef 2.N. Apiwanthanakorn, P. Supaphol, and M. Nithitanakul, Polym. Test. 23, 817 (2004).CrossRef 3.M. Xue, J. Sheng, Y. Yu, and H. H. Chuah, Eur. Polym. J. 40, 811 (2004).CrossRef 4.P. Supaphol, N. Dangseeyun, and P. Srimoaon, Polym. Test. 23, 175 (2004).CrossRef 5.G. Li, K. Wang, S. Li, and Y. Shi, J. Macromol. Sci. Part B: Phys. 46, 569 (2007).CrossRef 6.H. Liang, F. Xie, F. Guo, B. Chen, F. Luo, and Z. Jin, Polym. Bull. 60, 115 (2008).CrossRef 7.H. Chiu, Polym. Eng. Sci. 47, 2005 (2007).CrossRef 8.P. Supaphol, N. Apiwanthanakorn, and P. Krutphun, Polym. Test. 26, 985 (2007).CrossRef 9.M. Run, Y. Wang, C. Yao, and J. Gao, Thermochim. Acta. 447, 13 (2006).CrossRef 10.Z. Chen, C. Yao, and G. Yang, Polym. Test. 31, 393 (2012).CrossRef 11.H. Zou, L. Wang, C. Yi, and H. Gan, Polym. Int. 60, 1349 (2011).CrossRef 12.Z. Liu, K. Chen, and D. Yan, Eur. Polym. J. 39, 2359 (2003).CrossRef 13.X. Hu and A. J. Lesser, Macromol. Chemi. Phys. 205, 574 (2004).CrossRef 14.A. Gupta and V. Choudhary, Macromol. Symp. 290, 56 (2010).CrossRef 15.A. Gupta and V. Choudhary, J. Therm. Anal. Calorim. 114, 643 (2013).CrossRef 16.Y. Xu, S. Shang, and J. Huang, Polym. Test. 29, 1007 (2010).CrossRef 17.M. Avrami, J. Chem. Phys. 07, 1103 (1939).CrossRef 18.M. Avrami, J. Chem. Phys. 08, 212 (1940).CrossRef 19.M. Avrami, J. Chem. Phys. 09, 177 (1941).CrossRef 20.A. Jeziorny, Polymer 19, 1142 (1978).CrossRef 21.T. Ozawa, Polymer 12, 150 (1971).CrossRef 22.M. Liu, Q. Zhao, Y. Wang, C. Zhang, Z. Mo, and S. Cao, Polymer 44, 2537 (2003).CrossRef 23.H. E. Kissinger, J. Res. Nat. Bure. Stand. 57, 217 (1956).CrossRef 24.F. Chivrac, E. Pollet, and L. Averous, J. Polym. Sci. Part B: Polym. Phys. 45, 1503 (2007).CrossRef 25.M. Run, A. Song, Y. Wang, and C. Yao, J. Appl. Polym. Sci. 104, 3459 (2007).CrossRef 26.W. Xiaohui, S. Jun, C. Ying, F. Zhifeng, and S. Yan, China. Petro. Process. Petrochemi. Tech. 14, 74 (2012). 27.M. Eder, and A. Wlochowicz, Polymer 24, 1593 (1983).CrossRef 28.J. Yang, T. Zhao, J. Cui, L. Liu, Y. Zhou, G. Li, E. Zhou, and X. Chen, J. Polym. Sci. Part B: Polym. Phys. 44, 3215 (2006).CrossRef 29.J. Xiao, H. Zhang, X. Wan, D. Zhang, Q. Zhou, E. M. Woo, and S. R. Turner, Polymer 43, 3683 (2002).CrossRef 30.Z. Yang, and Z. Qiu, J. Appl. Polym. Sci. 119, 1426 (2011).CrossRef
作者单位:Suresh Dhandapani (1) S. K. Nayak (1) Smita Mohanty (2)
1. Advanced Research School for Technology and Product Simulation, Central Institute of Plastics Engineering and Technology, Tamil Nadu, Chennai, 600032, India 2. Laboratory for Advanced Research in Polymeric Materials, Central Institute of Plastics Engineering and Technology, Odisha, Bhubaneswar, 751024, India
刊物类别:Chemistry and Materials Science
刊物主题:Chemistry Polymer Sciences Russian Library of Science
出版者:MAIK Nauka/Interperiodica distributed exclusively by Springer Science+Business Media LLC.
ISSN:1555-6107
文摘
The blend of bio-based poly(trimethylene terephthalate)/poly(butylene adipate-co-terephthalate) blend (60/40 by weight ratio) was prepared via melt blending technique using twin screw extrusion. Its non-isothermal crystallization kinetics was investigated by differential scanning calorimetry at different cooling rate. Avrami and Ozawa model was utilized to investigate the crystal growth rate of the blend. The threedimensional crystal growth of the blend was changed into a two-dimensional one with increase of the cooling rate. The blend was crystallized in the form of non-banded spherulites with smaller crystal size. The crystallization activation energy of poly(trimethylene terephthalate) was reduced with the incorporation of poly(butylene adipate-co-terephthalate). The article is published in the original.