In-situ growth of ZnO particles on bamboo pulp fabric and its anti-UV property

详细信息    查看全文

• 作者：Guangyu Zhang (2)
  Hong Lin (1)
  Hideaki Morikawa (2)
  Mikihiko Miura (2)
  
• 关键词：Bamboo pulp fabric ; ZnO particles ; In ; situ ; Anti ; UV property
• 刊名：Fibers and Polymers
• 出版年：2013
• 出版时间：November 2013
• 年：2013
• 卷：14
• 期：11
• 页码：1803-1807
• 全文大小：
• 作者单位：Guangyu Zhang (2)
  Hong Lin (1)
  Hideaki Morikawa (2)
  Mikihiko Miura (2)
  
  2. Department of Bioscience and Textile Technology, Interdisciplinary Graduate School of Science and Technology, Shinshu University University, Ueda, 386-8567, Japan
  1. College of Textile and Costume Engineering, Soochow University, Suzhou, 215021, P.R. China
  
• ISSN：1875-0052

文摘

This research presents a simple way to enhance the anti-UV property of bamboo pulp fabric trough in situ synthesis of ZnO particles on the fabric. Bamboo Pulp Fabric was treated by immersion method in Zn(NO3)2 and multi-amide compound (RSD) aqueous solution under hydrothermal condition, then the ZnO particles were grown on the surface of bamboo pulp fabric by in-situ method. In this synthesis RSD was applied as a stabilizer, reactant and dispersant agent, the reaction mechanism was investigated. The ZnO particles were characterized by transmission electron microscope (TEM), Xray diffraction (XRD) and ultraviolet/visible light spectrophotometer. The anti-UV property of Bamboo Pulp Fabric was characterized by measuring its UPF. The results indicated that the diameter of ZnO is about 150 nm, the length is about 600 nm. The Bamboo Pulp Fabric treated with ZnO particles showed good anti-UV property and its UPF can reach to 83.59. After washing for 20 times, it can also keep good anti-UV property.