The analysis and fabrication of a novel tin-nickel mixed salt electrolytic coloured processing and the performance of coloured films for Al-12.7Si-0.7Mg alloy in acidic and alkali corrosive environments
详细信息 查看全文
- 作者：Yan Shang ; Changsheng Liu ; Carlos Fernandez…
- 关键词：Al ; 12.7Si ; 0.7Mg alloy ; Tin ; nickel mixed salt ; Electrolytic coloured ; Performance ; Corrosion resistance
- 刊名：International Journal of Precision Engineering and Manufacturing
- 出版年：2017
- 出版时间：January 2017
- 年：2017
- 卷：18
- 期：1
- 页码：93-98
- 全文大小：
- 刊物类别：Engineering
- 刊物主题：Industrial and Production Engineering; Materials Science, general;
- 出版者：Korean Society for Precision Engineering
- ISSN：2005-4602
- 卷排序：18
文摘
We present for the first time the analysis and fabrication of a novel Tin-Nickel mixed salt electrolytic coloured processing and the performance of coloured films for Al-12.7Si-0.7Mg alloy. This alloy is a novel alloy containing high silicon aluminum alloy extrusion profile which presents excellent mechanical properties as well as broad market prospects. Nevertheless, this kind of material is urgent in need of surface treatment technology. The orthogonal design and single factor tests were applied to optimize for electrolytic coloured technological conditions. By controlling operation conditions, the uniform electrolytic coloured films with different color were obtained. Analysis of microstructure showed that tin particles had been deposited in the coloured film. The coloured films, about 10 μm thick, were uniform, dense and firmly attached to the substrate. After the coloured samples were maintained at 400ºC for 1 h, or quenched from 300ºC to room temperature, the coloured films did not change, demonstrating excellent thermostability and thermal shock resistance. Acid and alkali corrosion tests and potentiodynamic polarization showed that corrosion resistance of coloured sample was much better than those of untreated samples. After 240 h neutral salt spray test, protection ratings and appearance ratings of coloured films were Grade 9.