Magnetic Properties of Nanocrystalline CoFe2O4/ZnFe2O4 Bilayers

详细信息    查看全文

• 作者：S. C. Sahoo (1)
  N. Venkataramani (2)
  Shiva Prasad (1)
  Murtaza Bohra (1) (3)
  R. Krishnan (4)
  
• 关键词：Ferrite bilayers ; Co ; ferrite ; Zn ; ferrite ; Magnetic properties ; Pulsed laser deposition
• 刊名：Journal of Superconductivity Incorporating Novel Magnetism
• 出版年：2012
• 出版时间：December 2012
• 年：2012
• 卷：25
• 期：8
• 页码：2653-2657
• 全文大小：274KB
• 参考文献：1. Bohra, M., Prasad, S., Kumar, N., Misra, D.S., Sahoo, S.C., Venkataramani, N., Krishnan, R.: Appl. Phys. Lett. 88, 262506 (2006) CrossRef
  2. Bohra, M., Prasad, S., Venkataramani, N., Kumar, N., Sahoo, S.C., Krishnan, R.: IEEE Trans. Mag. 47, 345 (2011) CrossRef
  3. Sahoo, S.C., Venkataramani, N., Prasad, S., Bohra, M., Krishnan,?R.: J. Nanosci. Nanotechnol. 10, 3112 (2010) CrossRef
  4. Ramos, A.V., Matzen, S., Moussy, J.-B., Ott, F., Viret, M.: Phys. Rev. B 79, 014401 (2009) CrossRef
  5. Suzuki, Y., van Dover, R.B., Gyorgy, E.M., Phillips, J.M., Felder, R.J.: Phys. Rev. B 53, 14016 (1996) CrossRef
  6. Margulies, D.T., Parker, F.T., Spada, F.E., Goldman, R.S., Li, J., Sinclair, R., Berkowitz, A.E.: Phys. Rev. B 53, 9175 (1996) CrossRef
  7. Dash, J., Prasad, S., Venkataramani, N., Krishnan, R., Kishan, P., Kumar, N., Kulkarni, S.D., Date, S.K.: J. Appl. Phys. 86, 3303 (1999) CrossRef
  8. Fullerton, E.E., Jiang, J.S., Grimsditch, M., Sowers, C.H., Bader, S.D.: Phys. Rev. B 58, 12193 (1998) CrossRef
  
• 作者单位：S. C. Sahoo (1)
  N. Venkataramani (2)
  Shiva Prasad (1)
  Murtaza Bohra (1) (3)
  R. Krishnan (4)
  
  1. Department of Physics, Indian Institute of Technology Bombay, Mumbai, 400076, India
  2. Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai, 400076, India
  3. Department of Physics, National Sun Yat-Sen University, Kaohsiung, 80424, Taiwan, Republic of China
  4. Groupe d’Etude de la Matière Condensée, CNRS/Universite de Versailles-St-Quentin, 78035, Versailles Cedex, France
  
• ISSN：1557-1947

文摘

Nanocrystalline spinel CoFe2O4/ZnFe2O4 bilayers were deposited by the pulsed laser deposition technique on amorphous fused quartz substrate at different substrate temperatures ranging from room temperature to 750?°C. The magnetic properties of the bilayers and of the single layer films deposited in identical conditions were studied at 300?K and at 10?K. Magnetic properties of the bilayers, in general, were found to be in between the individual values of the single layers. Magnetic measurements at 10?K clearly showed a two stepped magnetic hysteresis loop corresponding to the switching of the magnetic moments of the soft ZnFe2O4 and the hard CoFe2O4 layers. A study was also carried out by changing the thickness of ZnFe2O4 layer in the bilayer. This study showed that the magnetic properties of the bilayers even at room temperature can be controlled to some extent by changing the thickness of the soft ZnFe2O4 layer while maintaining a low substrate temperature of 350?°C.