文摘
The effect of thermo-mechanical treatment on the mechanical properties of a novel metastable β-type Ti-30Nb-1Mo-4Sn (wt?pct) alloy has been investigated. The solution-treated alloy consists of β and α-phases and exhibits a two-stage yielding with a low yield stress (around 100?MPa). After cold rolling at a reduction of 87.5?pct and subsequent annealing treat at 623?K (350?°C) for 30?minutes, a fine microstructure with nano-sized α precipitates distributed in small β grains as well as high density of dislocations was obtained to achieve a yield strength of 954?MPa and an ultimate tensile strength of 999?MPa. With low stability of β phase and small volume fraction of α precipitates, the annealed specimen exhibits a low Young’s modulus of 45?GPa. Such an excellent combination of the low elastic modulus and high strength in mechanical properties indicates a great potential candidate for biomedical applications.