Optimization and performance of cost-effective ultra-high performance concrete

详细信息    查看全文

• 作者：Weina Meng ; Mahdi Valipour ; Kamal Henri Khayat
• 刊名：Materials and Structures
• 出版年：2017
• 出版时间：February 2017
• 年：2017
• 卷：50
• 期：1
• 全文大小：764 KB
• 刊物类别：Engineering
• 刊物主题：Structural Mechanics
  Theoretical and Applied Mechanics
  Mechanical Engineering
  Operating Procedures and Materials Treatment
  Civil Engineering
  Building Materials
  
• 出版者：Springer Netherlands
• ISSN：1871-6873
• 卷排序：50

文摘

This paper presents a mix design method for ultra-high performance concrete (UHPC) prepared with high-volume supplementary cementitious materials and conventional concrete sand. The method involves the optimization of binder combinations to enhance packing density, compressive strength, and rheological properties. The water-to-cementitious materials ratio is then determined for pastes prepared with the selected binders. The sand gradation is optimized using the modified Andreasen and Andersen packing model to achieve maximum packing density. The binder-to-sand volume ratio is then determined based on the void content, required lubrication paste volume, and compressive strength. The optimum fiber volume is selected based on flowability and flexural performance. The high-range water reducer dosage and w/cm are then adjusted according to the targeted mini-slump flow and compressive strength. Finally, the optimized UHPC mix designs are evaluated to determine key properties that are relevant to the intended application. This mix design approach was applied to develop cost-effective UHPC materials. The results indicate that the optimized UHPC can develop 28-days compressive strength of 125 MPa under standard curing condition and 168–178 MPa by heat curing for 1 days Such mixtures have unit cost per compressive strength at 28 days of 4.1–4.5 $/m3/MPa under standard curing.KeywordsConventional concrete sandCost-effectiveMix designRheological propertiesSupplementary cementitious materials (SCMs)Ultra-high performance concrete (UHPC)