Mechanical properties of 2219-Al components produced by additive manufacturing with TIG
详细信息 查看全文
- 作者：J. Y. Bai ; C. L. Yang ; S. B. Lin ; B. L. Dong…
- 刊名：The International Journal of Advanced Manufacturing Technology
- 出版年：2016
- 出版时间：September 2016
- 年：2016
- 卷：86
- 期：1-4
- 页码：479-485
- 全文大小：2,963 KB
- 刊物类别：Engineering
- 刊物主题：Industrial and Production Engineering
Production and Logistics
Mechanical Engineering
Computer-Aided Engineering and Design - 出版者：Springer London
- ISSN：1433-3015
- 卷排序：86
文摘
Several 2219-Al components were produced by additive manufacturing with tungsten inert gas (TIG), and thin walls were selected to study the mechanical properties. Results show that the average hardness is 77.5 HV0.2, and the deposited materials are not sensitive to post heat during manufacturing process. No significant difference of hardness can be defined between strips and inner layers. Tensile tests were performed on welding and building directions. The average ultimate strength is 237 MPa, which is only 57 % of the property of 2219-T6 (routinely used state). Analysis suggests that the insufficiency of tensile strength can be ascribed to the absence of precipitation strengthening effect during the manufacturing process. The material exhibits an isotropic feature in tensile properties. Fracture observation shows that θ phases are the initiations of cracks. The effect of decreasing loading areas, due to the strip-like distributing porosities, is insignificant in welding direction. However, in building direction, it influences the crack propagating path.KeywordsAdditive manufacturing2219-AlMechanical propertiesTIG