Effects of strain rate on stress corrosion of S355 steel in 3.5% NaCl solutions

详细信息    查看全文

• 作者：Yifu Jin 金亦富 ; Tianyuan Sheng ; Weicheng Kong…
• 关键词：Key wordsstrain rate ; slow strain rate test ; S355 steel ; stress corrosion ; fracture morphology
• 刊名：Journal of Wuhan University of Technology-Mater. Sci. Ed.
• 出版年：2016
• 出版时间：December 2016
• 年：2016
• 卷：31
• 期：6
• 页码：1381-1386
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Materials Science, general;
• 出版者：Wuhan University of Technology
• ISSN：1993-0437
• 卷排序：31

文摘

The stress corrosion of S355 steel in 3.5% NaCl solution under the different strain rates was analyzed with the slow strain rate test (SSRT), the stress corrosion cracking (SCC) behaviors of S355 steel under the different strain rates in the solution were investigated, and the fracture morphologies and compositions of corrosion products under the different strain rates were analyzed with scanning electron microscopy (SEM) and energy dispersive spectrometerry (EDS), respectively. The experimental results show that the SCC sensitivity index is the highest when the strain rate is 2×10-6, and the medium corrosion is the main reason resulting in the highest SCC sensitivity index. The SCC sensitivity index is the least when the strain rate is 5×10-6, and the stress is the main reason resulting in the stress corrosion. The SCC sensitivity index is the middle when the strain rate is 9×10-6, the interaction of stress and medium is the stress corrosion fracture mechanism.