参考文献:1.Klueh R L, and Nelson A T, J Nucl Mater 371 (2007) 37.CrossRef 2.Sakthivel T, Laha K, Parameswaran P, Panneer Selvi S, Chandravathi K S, and Mathew M D, Trans Indian Inst Met 68 (2015) 411.CrossRef 3.Vitek J M, and Klueh R L, Metall Trans 14 (1983) 1047.CrossRef 4.Liu C, Zhang D, Liu Y, and Yan Z, Nucl Eng Des 241 (2011) 2411.CrossRef 5.Zeman A, Debarberis L, Kock J, Slugen V, and Keilova E, J Nucl Mater 362 (2007) 259.CrossRef 6.Moitra P, Sreenivasan R, Mannan S L, and Singh V, Metall Mater Trans A 36 (2005) 2957.CrossRef 7.Laha K, Saroja S, Moitra A, Sandhya R, Mathew M D, Jayakumar T, and Rajendra Kumar E, J Nucl Mater 439 (2013) 41.CrossRef 8.Bhattacharjee D, and Davis C L, Scr Mater 47 (2002) 825.CrossRef 9.Takaki S, Kawasaki K, and Kimura Y, J Mater Process Technol 117 (2001) 359.CrossRef 10.Megusar J, Lavernia E, Domalavage P, Harling O K, and Grant N J, J Nucl Mater 122–123 (1984) 789.CrossRef 11.Wang C, Wang M, Shi J, Hui W, and Dong H, Scr Mater 58 (2008) 492.CrossRef 12.Karthikeyan T, Thomas Paul V, Saroja S, Moitra A, Sasikala G, and Vijayalakshmi M, J Nucl Mater 419 (2011) 256.CrossRef 13.Gaoa Q, Liua Y, Dia X, Yua L, Yana Z, and Qiao Z, Nucl Eng Des 256 (2013) 148.CrossRef 14.Obara S, Wakai T, Asayama T, Yamada Y, and Nakazawa T, Tetsu-to-Hagane 95 (2009) 31. 15.Ennis P J, Zielinska-Lipiec A, Wachter O, and Czyrska-Filemonowicz A, Acta Mater 45 (1997) 4901. 16.Sakthivel T, Panneer Selvi S, and Laha K, Mater Sci Eng A 640 (2015) 61.CrossRef 17.Kocks U F, and Mecking H, Prog Mater Sci 48 (2003) 171.CrossRef 18.Isaac Samuel E, Choudhary B K, and Bhanu Sankara Rao K, Scr Mater 46 (2002) 50713. 19.Kellera C, Margulies M M, Hadjem-Hamouche Z, and Guillot I, Mater Sci Eng A 527 (2010) 6758.CrossRef 20.Chandravathi K S, Sasmal C S, Laha K, Parameswaran P, Nandagopal M, Vijayanand V D, Mathew M D, Jayakumar T, and Rajendra Kumar E, J Nucl Mater 435 (2013) 128.CrossRef
作者单位:S. Panneer Selvi (1) T. Sakthivel (1) P. Parameswaran (1) K. Laha (1)
1. Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603 102, India
刊物类别:Chemistry and Materials Science
刊物主题:Materials Science Metallic Materials Materials Science, general Tribology, Corrosion and Coatings
出版者:Springer India
ISSN:0975-1645
文摘
Creep and tensile properties have been investigated on modified 9Cr–1Mo steel subjected to single and double normalization heat treatments. Optical, scanning and transmission electron microscopic investigations revealed the presence of finer prior austenite grain size and coarsening of MX precipitates in the double normalized steel as compared to the steel subjected to single normalization heat treatment. Increased minimum creep rate and significant reduction in creep rupture life were observed in the double normalized steel. Increased tensile ductility coupled with marginal decrease in tensile strength was observed with double normalized steel compared to single normalized steel. The double normalized steel exhibited lower creep strength and higher tensile ductility than the single normalized steel. Keywords Grade 91 ferritic steel Heat treatment Creep Tensile