Lead Sulfide Cathode for Quantum Dot Solar Cells: Electrosynthesis and Characterization

详细信息    查看全文

• 作者：Nghiem Van Le ; Hoang Thai Nguyen ; Hai Viet Le…
• 关键词：Cyclic voltammetry ; electrodeposition ; lead sulfide ; quantum dot ; solar cell
• 刊名：Journal of Electronic Materials
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：46
• 期：1
• 页码：274-281
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Optical and Electronic Materials; Characterization and Evaluation of Materials; Electronics and Microelectronics, Instrumentation; Solid State Physics;
• 出版者：Springer US
• ISSN：1543-186X
• 卷排序：46

文摘

Deposition of lead sulfide (PbS) nanocrystalline thin films onto conducting fluorine-doped tin oxide (FTO) glass has been performed by cyclic voltammetry (CV) in 1.5 mM solution of lead nitrate and sodium thiosulfate at 100 mV s−1 scan rate in the potential range of −1.0 V to 0.0 V versus saturated calomel electrode. X-ray diffraction analysis and scanning electron microscopy revealed formation of cubic PbS crystals with size of 100 nm to 150 nm after 50 cycles. High electrocatalytic activity of the synthesized PbS film for the S2−/S_n2− redox couple, used as a mediator for quantum dot solar cells (QDSCs), was demonstrated by electrochemical impedance spectroscopy and CV measurements. The prepared PbS/FTO was used as a counterelectrode to fabricate PbS-QDSCs with a photoanode consisting of CdS/CdSe quantum dots adsorbed on mesoporous TiO₂ film and a polysulfide solution electrolyte. The performance of the PbS-QDSC was compared with a QDSC with a platinum counterelectrode (Pt-QDSC). It was found that, using the same fabrication conditions, the performance of the PbS-QDSC was better than that of the Pt-QDSC. At 1 sun (100 mW cm−2) simulated light, average energy conversion efficiency of 2.14%, short-circuit current of 9.22 mA cm−2, open-circuit potential of 0.50 V, and fill factor of 0.47 were achieved by the fabricated PbS-QDSC.