S segregation at the α/γ interface remains in duplex stainless steel with only 10 ppm S. The interfacial brittle tearing appears during hot deformation due to S segregation. Minor rare earth additions can effectively eliminate the S contamination. In particular, RE enrichment at the α/γ interface indicating its microalloying effect is an important cause. Manuscript submitted March 21, 2015.