Surface morphology and thermal figure of merit of a new compound thin film
详细信息 查看全文
- 作者：Hussain A. Badran ; Hassan A. Sultan…
- 刊名：Journal of Materials Science: Materials in Electronics
- 出版年：2016
- 出版时间：July 2016
- 年：2016
- 卷：27
- 期：7
- 页码：6735-6744
- 全文大小：1,720 KB
- 刊物类别：Chemistry and Materials Science
- 刊物主题：Chemistry
Optical and Electronic Materials
Characterization and Evaluation Materials - 出版者：Springer New York
- ISSN：1573-482X
- 卷排序：27
文摘
The third nonlinear optical properties of a new compound 4,4′-bis(3-methoxy benzylidene amino) biphenyl doped poly-methyl methacrylate (PMMA) have been studied using Z-scan technique. Experiments are performed using a continuous waveguide (cw) diode laser at 532 nm wavelength and 0.68 kW/cm2 laser intensity. The optical power limiting behavior of sample doped PMMA was also investigated. It also shows a very good optical limiting behavior with a limiting threshold of 4.7 mW. We attribute the nonlinear absorption and optical limiting property of the sample film to two photon absorption effect at 532 nm. The experimental evidences of observing diffraction pattern in compound 4,4′-bis(3-methoxybenzylideneamino) biphenyl doped PMMA has been present. The refractive index change, Δn, and nonlinear refractive index, n2 determined from the number of observed ring. We obtained good values of Δn = 105.154 × 10−4and n2 = 154.154 × 10−7 cm2/W. Variation of refractive index with temperature, dn/dT, and figure of merit, H, are found to be 8.858 × 10−6 1/°C and 5.316 × 10−6, respectively. This large nonlinearity is attributed to a thermal effect resulting from linear absorption. Theoretical diffraction pattern that agree well with experimental one are generated using a wave theory.