Study on the chain entanglement of polyvinyl alcohol fiber during the dry-jet wet spinning process

详细信息    查看全文

• 作者：Yin Zhu (1)
  Chengxun Wu (1)
  Youwei Zhang (1)
  Jiongxin Zhao (1)
  
  1. State Key Laboratory for Modification of Chemical Fibers and Polymer Materials ; College of Material Science and Engineering ; Donghua University ; Shanghai ; 201620 ; China
  
• 关键词：Polyvinyl alcohol ; Entanglement ; Polarizing thermomicroscope ; Swelling DSC ; High strength fiber
• 刊名：Fibers and Polymers
• 出版年：2015
• 出版时间：February 2015
• 年：2015
• 卷：16
• 期：2
• 页码：345-353
• 全文大小：575 KB
• 参考文献：1. Gasilova, E., Benyahia, L., Durand, D., Nicolai, T. (2002) Macromolecules 35: pp. 141 CrossRef
  2. Rosa, A., Orlandini, E., Tubiana, L., Micheletti, C. (2011) Macromolecules 44: pp. 8668 CrossRef
  3. Rong, W. R., Fan, Z. Y., Yu, Y., Bu, H. S., Wang, M. (2005) J. Polym. Sci. Pt. B-Polym. Phys. 43: pp. 2243 CrossRef
  4. Bernazzani, P., Simon, S. L., Plazek, D. J., Ngai, K. L. (2002) Eur. Phys. J. E 8: pp. 201 CrossRef
  5. Bu, H. S., Gu, F. M., Bao, L. R., Chen, M. (1998) Macromolecules 31: pp. 7108 CrossRef
  6. Tsui, O. K. C., Zhang, H. F. (2001) Macromolecules 34: pp. 9139 CrossRef
  7. Bartczak, Z. (2005) Macromolecules 38: pp. 7702 CrossRef
  8. Ikeda, Y., Ohta, T. (2008) Polymer 49: pp. 621 CrossRef
  9. Heinrich, G., Vilgis, T. A. (1993) Macromolecules 26: pp. 1109 CrossRef
  10. Bueche, F. J. (1962) Physical Properties of Polymers. Interscience Publishers, New York
  11. Gennes, P.-G. D. (1979) Scaling Concepts in Polymer Physics. Cornell University Press, New York
  12. Kosc, M. (1988) Colloid Polym. Sci. 266: pp. 105 CrossRef
  13. Wu, S. (1989) J. Polym. Sci. Pt. B-Polym. Phys. 27: pp. 723 CrossRef
  14. Colby, R. H., Rubinstein, M., Viovy, J. L. (1992) Macromolecules 25: pp. 996 CrossRef
  15. Brown, H. R., Russell, T. P. (1996) Macromolecules 29: pp. 798 CrossRef
  16. Heymans, N. (2000) Macromolecules 33: pp. 4226 CrossRef
  17. Litvinov, V. M., Ries, M. E., Baughman, T. W., Henke, A., Madoka, P. P. (2013) Macromolecules 46: pp. 541 CrossRef
  18. Saalwachter, K. (2013) Macromolecules 46: pp. 5090 CrossRef
  19. Litvinov, V. M., Ries, M. E., Baughman, T. W., Henke, A., Matloka, P. P. (2013) Macromolecules 46: pp. 5094 CrossRef
  20. Babu, A. R., Gundiah, N. (2014) Exp. Mech. 54: pp. 1177 CrossRef
  21. Nilsson, F., Lan, X., Gkourmpis, T., Hedenqvist, M. S., Gedde, U. W. (2012) Polymer 53: pp. 3594 CrossRef
  22. Schieber, J. D., Indei, T., Steenbakkers, R. J. A. (2013) Polymers-Basel 5: pp. 643 CrossRef
  23. Qian, R. Y. (1997) Macromol. Symp. 124: pp. 15 CrossRef
  24. Qin, J., Hu, P. P., Zhao, J. X., Wu, Z. Q., Qian, B. J. (1994) J. Appl. Polym. Sci. 51: pp. 1433 CrossRef
  25. Qian, B. J., Hu, P. P., He, J. M., Zhao, J. X., Wu, C. X. (1992) Polym. Eng. Sci. 32: pp. 1290 CrossRef
  26. Qian, B. J., Wu, Z. Q., Hu, P. P., Qin, J., Wu, C. X., Zhao, J. X. (1991) J. Appl. Polym. Sci. 42: pp. 1155 CrossRef
  27. Qian, B. J., Wu, Z. Q., Hu, P. P., Qin, J., Wu, C. X., Zhao, J. X. (1993) J. Appl. Polym. Sci. 47: pp. 1881 CrossRef
  28. Qian, B. J., Qin, J., Wu, Z. Q., Wu, C. X., Hu, P. P., Zhao, J. X. (1992) J. Appl. Polym. Sci. 45: pp. 871 CrossRef
  29. Qian, B., Zhu, J., He, J., Hu, P., Wu, C. (1994) J. Appl. Polym. Sci. 53: pp. 1261 CrossRef
  30. Liu, M. Z., Cheng, R. S., Wu, C., Qian, R. Y. (1997) J. Polym. Sci. Pt. B-Polym. Phys. 35: pp. 2421 CrossRef
  31. Jo, Y. G., Shin, E. J., Lee, Y. J., Yoon, W. S., Han, S. S., Lee, Y. H., Lee, Y. R., Noh, S. K., Gal, Y. S., Lyoo, W. S. (2009) J. Appl. Polym. Sci. 113: pp. 1733 CrossRef
  32. Lu, Y. Y., An, L. J., Wang, S. Q., Wang, Z. G. (2013) Acs Macro. Lett. 2: pp. 561 CrossRef
  33. Wang, Y. Y., Li, X., Zhu, X. Y., Wang, S. Q. (2012) Macromolecules 45: pp. 2514 CrossRef
  
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Chemistry
  Polymer Sciences
  
• 出版者：The Korean Fiber Society
• ISSN：1875-0052

文摘

The entanglement structure of polyvinyl alcohol (PVA) fiber during the dry-jet wet spinning process is studied in this article. The morphological changes of PVA fiber in swelling agent are observed under optical polarizing thermomicroscope, and the entanglement changes of PVA fiber during the spinning process are investigated using swelling DSC method. A specific mixture consisting of a good solvent (DMSO) and a poor solvent (EG) is used as the swelling agent for PVA. Results show that the entanglement structure of PVA fiber would disentangle after the crystalline phase is destroyed in the swelling agent during heating, and the entanglement structure of PVA fiber is greatly dependent on the spinning technological parameters such as spinning dope concentration, jet stretch ratio, extruding shear stress and draw ratio of the whole spinning process. When the spinning dope and spinning technological parameters are controlled properly, the entanglement structure in the PVA fiber can be greatly reduced and PVA fiber with a 17.5 cN/dtex tensile strength can be obtained.