参考文献:1. R.W. Sandelin: Wire Wire Prod., 1940, vol. 15, pp. 655-6. 2. H. Guttman and P. Niessen: Can. Metall. Q., 1972, vol. 11, pp. 609-5. CrossRef 3. A.R.B. Verma and W.J. van Ooij: Surf. Coat. Technol., 1997, vol. 89, pp. 132-2. CrossRef 4. A.R.P. Ghuman and J.L. Goldstein: Metall. Trans., 1971, vol. 2, pp. 2903-4. CrossRef 5. Y.X Liu, F.C. Yin, H. Tu, Z. Li, J.H. Wang, and X.P. Su: J. Phase Equilib., 2008, vol. 29, pp. 493-9. CrossRef 6. Z. Li, X.P Su, and Y. He: J. Alloys Compd., 2008, vol. 462, pp. 320-7. CrossRef 7. X.H Tang, F.C Yin, X.M Wang, J.H Wang, and X.P Su: / J. Phase Equilib., 2007, vol. 28, pp. 355-1. 8. F.G. Li, F.C. Yin, X.P. Su, and Z. Li: Chin. J. Nonferrous Met., 2010, vol. 20, pp. 86-1. 9. M.X. Zhao, F.C. Yin, Z. Li, Z.H. Long, and X.M. Wang: Int. J. Mater. Res., 2013, vol. 104, pp. 35-5. CrossRef 10. K. Zhang and N.Y. Tang: Metall. Mater. Trans. A, 2003, vol. 34A, pp. 2387-6. CrossRef 11. X.P. Su, F.C. Yin, Z. Li, N.Y. Tang, and M.X. Zhao: J. Alloys Compd., 2005, vol. 396, pp. 156-3. CrossRef 12. C.S. Sha, S.H. Liu, Y. Du, H.H Xu, L.J. Zhang, and Y.Q. Liu: CALPHAD, 2010, vol. 34, pp. 405-4. CrossRef 13. G.V. Raynor and V.G. Rivlin: / Phase Equilibria in Iron Ternary Alloys, Institute of Metals, London, 1988. 14. M.X. Zhao, F.C. Yin, X.Q. Li, Z. Li, and Z.H. Long: J. Alloys Compd., 2012, vol. 540, pp. 215-1. CrossRef 15. V. Raghavan: J. Phase Equilib., 2003, vol. 24, pp. 551-3. CrossRef 16. K. Ishida, T. Nishizawa, and M. Schlesinger: J. Phase Equilib., 1991, vol. 12, pp. 578-6. CrossRef 17. L. Kaufman: CALPHAD, 1979, vol. 3, pp. 275-1. CrossRef 18. L. Zhang, Y. Du, H. Xu, and Z. Pan: CALPHAD, 2006, vol. 30, pp. 470-1. CrossRef 19. T.B. Massalski, H. Okamoto, P.R. Subramanian, and L. Kacprzak: Binary Alloy Phase Diagrams, 2nd ed., ASM, Materials Park, OH, 1990. 20. M. Hansen and K. Anderko: Constitution of Binary Alloys, 2nd ed., McGraw-Hill, New York, NY, 1958. 21. I. Isom?ki and M. H?m?l?inen: J. Alloys Compd., 2004, vol. 375, pp. 191-5. CrossRef 22. G.P. Vassilev and M. Jiang: J. Phase Equilib., 2004, vol. 25, pp. 259-8. CrossRef 23. M.H.G. Jacobs and P.J. Spencer: CALPHAD, 1996, vol. 20, pp. 307-0. CrossRef 24. A.T. Dinsdale: CALPHAD, 1991, vol. 15, pp. 317-25. CrossRef 25. O. Redlich and A. Kister: Ind. Eng. Chem., 1948, vol. 40, pp. 345-8. CrossRef 26. M. Hillert and M. Jarl: CALPHAD, 1978, vol. 2, pp. 227-8. CrossRef
作者单位:Weilin Wang (1) Fucheng Yin (1) Manxiu Zhao (1) Zhi Li (1) Yu Wu (1)
1. Key Laboratory of Materials Design and Preparation Technology, Xiangtan University, Xiangtan, 411105, P.R. China
ISSN:1543-1940
文摘
Phase relations of the Co-Si-Zn ternary system were experimentally investigated and thermodynamically calculated. First, the isothermal sections of the Co-Si-Zn system at 1123?K and 1323?K (850 °C and 1050 °C) were investigated experimentally using scanning electron microscopy coupled with wave-dispersive X-ray spectroscopy and X-ray diffraction. Then the thermodynamic calculation for this system was carried out using the CALPHAD technique. The calculated results and the experimental data are reasonably self-consistent.