参考文献:1. Aric貌 AS, Srinivasan S, Antonucci V (2001) Fuel Cells 1(2):133 CrossRef 2. Gottesfeld S (2007) J Power Sources 171(1):37 CrossRef 3. Watanabe M, Motoo S (1975) J Electroanal Chem 60(3):267 CrossRef 4. Seiler T, Savinova ER, Friedrich KA et al (2004) Electrochim Acta 49(22鈥?3):3927 CrossRef 5. Lu GQ, Chrzanowski W, Wieckowski A (2000) J Phys Chem B 104(23):5566 CrossRef 6. Waszczuk P, Solla-Gull贸n J, Kim HS et al (2001) J Catal 203(1):1 CrossRef 7. Gojkovi膰 SLJ, Vidakovi膰 TR, 脨urovi膰 DR (2003) Electrochim Acta 48(24):3607 CrossRef 8. Pope MT, Muller A (1991) Angew Chem Int Ed 30(1):34 CrossRef 9. Pan DW, Chen JH, Tao WY et al (2006) Langmuir 22(13):5872 CrossRef 10. Garrigue P, Delville MH, Labrug猫re C et al (2004) Chem Mater 16(16):2984 CrossRef 11. Cui Z, Kulesza PJ, Li CM (2011) Int J Hydrogen Energy 36(14):8508 CrossRef 12. Wang D, Lu S, Xiang Y et al (2011) Appl Catal B 103(3鈥?):311 13. Seo MH, Choi SM, Kim HJ et al (2008) J Power Sources 179(1):81 CrossRef 14. Ferrell JR III, Kuo KC, Turner JA et al (2008) Electrochim Acta 53(14):4927 CrossRef 15. Han DM, Guo ZP, Zhao ZW et al (2008) J Power Sources 184(2):361 CrossRef 16. Guo ZP, Han DM, Wexler D et al (2008) Electrochim Acta 53(22):6410 CrossRef 17. Guo X, Guo DJ, Wang JS et al (2010) J Electroanal Chem 638(1):167 CrossRef 18. Otomo J, Li X, Kobayashi T et al (2004) J Electroanal Chem 573:99 CrossRef 19. Mueller JT, Urban PM (1998) J Power Sources 75:139 CrossRef 20. M眉ller JT, Urban PM, H枚lderich WF (1999) J Power Sources 84:157 CrossRef 21. Hsing IM, Wang X, Leng YJ (2002) J Electrochem Soc 149(5):A615 CrossRef 22. Kim WB, Voitl T, Rodriguez-Rivera GJ (2004) Science 305(5688):1280 CrossRef 23. Kulesza PJ, Chojak M, Karnicka K et al (2004) Chem Mater 16(21):4128 CrossRef 24. Chojak M, Kolary-Zurowska A, Wlodarczyk R et al (2007) Electrochim Acta 52(18):5574 CrossRef
作者单位:Weimin Chen (1) Xufang Wei (1) Yu Zhang (1)
1. School of Environmental and Chemical Engineering, Shenyang Ligong University, Shenyang, 110159, China
ISSN:1572-8838
文摘
Phosphomolybdic acid (H3PMo12O40, PMo12) was employed to modify PtRu nanocatalysts for methanol electro-oxidation. The results show that the performance of PtRu catalysts was improved by the formation of the negatively charged self-assembled PMo12 monolayer on the catalyst surface. Electrochemical measurements indicate that the PMo12-modified PtRu catalyst has a higher catalytic activity and a better poison tolerance than the unmodified one. It is also found that the sequence in which PtRu and PMo12 were deposited onto the carbon support during the preparation process has a major influence on the performance of PMo12-modified PtRu nanocatalysts. X-ray photoelectron spectra results show that the self-assembled PMo12 layer inhibits the formation of metal oxides/hydroxides on the surface of PtRu nanoparticles to some extent.