Hybrid laminated composites molded by spray lay-up process

详细信息    查看全文

• 作者：Bing Xiao ; Yuqiu Yang ; Xiaofeng Wu ; Mengyuan Liao ; Ryuiti Nishida…
• 关键词：Spray lay ; up ; Laminated interfacial property ; Glass fiber ; Jute fiber ; Bending stiffness
• 刊名：Fibers and Polymers
• 出版年：2015
• 出版时间：August 2015
• 年：2015
• 卷：16
• 期：8
• 页码：1759-1765
• 全文大小：772 KB
• 参考文献：1.A. K. Bledzki and J. Gassan, Prog. Polym. Sci., 24, 221 (1999).CrossRef
  2.S. Carmisciano, I. M. De Rosa, F. Sarasini, A. Tamburrano, and M. Valente, Mater. Des., 32, 337 (2011).CrossRef
  3.C. W. Chin and B. F. Yousif, Wear, 267, 1550 (2009).CrossRef
  4.S. K. Garkhail, R. W. H. Heijenrath, and T. Peijs, Appl. Compos. Mater., 7, 351 (2000).CrossRef
  5.B. F. Yousif and H. Ku, Mater. Des., 36, 847 (2012).CrossRef
  6.K. S. Ahmed, S. Vijayarangan, and A. C. B. Naidu, Mater. Des., 28, 2287 (2007).CrossRef
  7.A. N. Netravali and S. Chabba, Mater. Today, 6, 22 (2003).CrossRef
  8.B. V. Ramnath, R. Sharavanan, M. Chandrasekaran, C. Elanchezhian, R. Sathyanarayanan, R. N. Raja, and S. J. Kokan, Fiber. Polym., 16, 164 (2015).CrossRef
  9.S. Siddika, F. Mansura, M. Hasan, and A. Hassan, Fiber. Polym., 15, 1023 (2014).CrossRef
  10.A. Stocchi, B. Lauke, M. I. Giannotti, A. Vazquez, and C. Bernal, Fiber. Polym., 14, 285 (2013).CrossRef
  11.N. Venkateshwaran and A. ElayaPerumal, Fiber. Polym., 13, 907 (2012).CrossRef
  12.G. M. Shafiur Rahman, M. A. Al Mamun, and M. A. Khan, Fiber. Polym., 15, 340 (2014).CrossRef
  13.M. R. Rahman, M. M. Huque, M. N. Islam, and M. Hasan, Compos. Pt. A-Appl. Sci. Manuf., 39, 1739 (2008).CrossRef
  14.K. S. Ahmed and S. Vijayarangan, J. Mater. Process. Technol., 207, 330 (2008).CrossRef
  15.K. S. Ahmed, S. Vijayarangan, and C. Rajput, J. Reinf. Plast. Compos., 25, 1549 (2006).CrossRef
  16.H. M. Akil, I. M. De Rosa, C. Santulli, and F. Sarasini, Mater. Sci. Eng., 527, 2942 (2010).CrossRef
  17.S. Thitithanasarn, K. Yamada, U. S. Ishiaku, and H. Hamada, J. Appl. Polym. Sci., 127, 2952 (2013).CrossRef
  18.A. Stocchi, L. Colabella, A. Cisilino, and V. 脕lvarez, Mater. Des., 55, 394 (2014).CrossRef
  19.C. Wang, P. Uawongsuwan, Y. Yang, and H. Hamada, Polym. Eng. Sci., 53, 1657 (2013).CrossRef
  20.Y. Yang, M. Murakami, and H. Hamada, J. Polym. Environ., 20, 1124 (2012).CrossRef
  21.Y. Yang, Y. Yu, T. Ota, Y. Tanaka, R. Nishida, S. Kawabata, and H. Hamada, Polym. Polym. Compos., 19, 197 (2011).
  22.Y. Yang, T. Ota, T. Morii, and H. J. Hamada, Mater. Sci., 46, 2678 (2011).CrossRef
  
• 作者单位：Bing Xiao (1)
  Yuqiu Yang (1) (2)
  Xiaofeng Wu (3)
  Mengyuan Liao (4)
  Ryuiti Nishida (4)
  Hiroyuki Hamada (4)
  
  1. Department of Textile Engineering, College of Textiles, Donghua University, Shanghai, 201620, China
  2. Key Laboratory of Textile Science & Technology, Ministry of Education, College of Textiles, Donghua University, Shanghai, 201620, China
  3. Department of Electronic Engineering, School of Information Science and Technology, Fudan University, Shanghai, 200433, China
  4. Advanced Fibro-science, Kyoto Institute of Technology, Kyoto, 606-8585, Japan
  
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Chemistry
  Polymer Sciences
  
• 出版者：The Korean Fiber Society
• ISSN：1875-0052

文摘

At current study, several layers were laminated by spray-up method by using the same materials as bath tub products fabrication. The bending properties of laminated plate together with the separated acrylic resin, glass reinforced unsaturated polyester layer (GFRP) layers were investigated by 3 point bending test. And acoustic emission (AE) was measured simultaneously. It is found that GFRP contribute to the high bending modulus and the laminated bonding property is high based on the short beam bending test. Similarly, AE result shows the fracture or delamination were generated with the glass fiber fracture simultaneously which support the conclusion that the laminated fracture did not generated early than other fractures. Finally, the calculation were carried out in order to use recycled jute woven fabric reinforced unsaturated polyester layer (JFRP) instead of GFRP. The bending property of the laminated plate with JFRP was tested as compared with the one consisting GFRP. Keywords Spray lay-up Laminated interfacial property Glass fiber Jute fiber Bending stiffness