Improved mechanical and barrier properties of PPC multilayer film through interlayer hydrogen bonding interaction
详细信息 查看全文
- 作者：Tungalag Dong (1)
Xueyan Yun (1)
Cancan Shi (1) (2)
Wenxiu Sun (1)
Guisheng Fan (1)
Ye Jin (1) - 刊名：Polymer Science Series A
- 出版年：2014
- 出版时间：November 2014
- 年：2014
- 卷：56
- 期：6
- 页码：830-836
- 全文大小：404 KB
- 参考文献：1. M. H. Chisholm, D. Navarro-Llobet, and Z. Zhou, Macromolecules 35, 6494 (2002). CrossRef
2. M. H. Chisholm and Z. Zhou, J. Am. Chem. Soc. 126, 11030 (2004). CrossRef
3. G. A. Luinstra, Polym. Rev. 48, 192 (2008). CrossRef
4. O. Iwao, Catal. Today 115, 33 (2006). CrossRef
5. D. J. Darensbourg, M. Ulusoy, O. Karroonnirun, et al., Macromolecules 42, 6992 (2009). CrossRef
6. A. Rokicki and W. J. Kuran, J. Macromol. Sci., Rev. Macromol. Chem. 21, 135 (1981).
7. J. Jiao, M. Xiao, D. Shu, et al., J. Appl. Polym. Sci. 102, 5240 (2006). CrossRef
8. S.D. Allen, D. R. Moore, E. B. Lobkovsky, and G. W. Coates, J. Am. Chem. Soc. 124, 14284 (2002). CrossRef
9. P. Gorecki and W. Kuran, J. Polym. Sci., Polym. Lett. Ed. 23, 299 (1985). CrossRef
10. X. C. Ge, Y. Xu, and Y. Z. Meng, Compos. Sci. Technol. 65, 2219 (2005). CrossRef
11. X. B. Lu and Y. Wang, Angew. Chem., Int. Ed. Engl. 43, 3574 (2004). CrossRef
12. J. Xu, R. K. R. Li, Y. Z. Meng, and Y. W. Mai, Mater. Res. Bull. 41, 244 (2006). CrossRef
13. X. F. Ma, J. G. Yu, and A. Zhao, Compos. Sci. Technol. 66, 2360 (2006). CrossRef
14. X. Shi and Z. Gan, Eur. Polym. J. 43, 4852 (2007). CrossRef
15. J. Tao, C. Song, M. Cao, et al., Polym. Degrad. Stab. 94, 575 (2009). CrossRef
16. J. Seo, G. Jeon, E. S. Jang, et al., J. Appl. Polym. Sci. 122, 1101 (2011). CrossRef
17. C. Barreto, J. Proppe, S. Fredriksen, et al., Polymer 54, 3574 (2013). CrossRef
18. F. Shahidi, J. K. V. Arachchi, and Y. J. Jeon, Trends Food Sci. Technol. 10, 37 (1999). CrossRef
19. A. Khan, R. A. Khan, S. Salmieri, et al., Carbohydr. Polym. 90, 1601 (2012). CrossRef
20. M. G?llstedt and M. S. Hedenqvist, Carbohydr. Polym. 63, 46 (2006). CrossRef
21. K. J. Kim and J. L. White, Compos. Interfaces 16, 619 (2009). Xueyan Yun (1)
Cancan Shi (1) (2)
Wenxiu Sun (1)
Guisheng Fan (1)
Ye Jin (1)
1. College of Food Science and Engineering, Inner Mongolia Agricultural University, 306 Zhaowuda Road. Hohhot, Inner Mongolia, 010018, China
2. Engineering College, Northeast Agricultural University, No. 59 Mucai Street Xiangfang District, Harbin, 150030, China - ISSN：1555-6107
文摘
Poly(propylene carbonate) (PPC) is coated with cellophane (PT) via the intermolecular hydrogen bonds of chitosan (CS) with the both polymers, and their multilayer films are prepared in different weight ratios. The trace presence of chitosan on the surface of PT promotes the combination with PPC layers. After coating, the Young’s modulus and tensile strength of PPC are greatly improved, the storage modulus still keep a high value between ?-0°C. The oxygen barrier of PPC is increased at least 580 times, and the multilayer films still keep good water vapor barrier in some degree.