参考文献:1. Mahan G D. Solid State Phys, 1998, 51: 81-57 CrossRef 2. Vining C B, Bell L E. Science, 2008, 321: 1457-461 CrossRef 3. Terasaki I, Sasago Y, Uchinokura K. Phys Rev B, 1997, 56: 12685-2687 CrossRef 4. Hossain M S, Islam R, Shahjahan M, et al. J Mater Sci Mater Electron, 2008, 19: 1114-121 CrossRef 5. Ohta S, Nomura T, Ohta H, et al. J Appl Phys, 2005, 97: 034106 CrossRef 6. Androulakis J, Migiakis P, Giapintzakis J. Appl Phys Lett, 2004, 84: 1099-101 CrossRef 7. Berardan D, Byl C, Dragoe N. J Am Ceram Soc, 2010, 93: 2352-358 CrossRef 8. Li F, Li J F. Ceram Int, 2011, 37: 105-10 CrossRef 9. Park K, Jang K U, Kwon H C, et al. J Alloys Compd, 2006, 419: 213-19 CrossRef 10. Wang H Q, Hua Z Q, Peng S J, et al. Physica B, 2011, 406: 4183-187 CrossRef 11. Wang H Q, Hua Z Q, Peng S J, et al. Ceram Int, 2012, 38: 1133-137 CrossRef 12. Dong X, Wang H Q, Hua Z Q, et al. J Mater Sci, 2012, 23: 1210-214 13. Wang Y, Yao K L, Liu Z L. J Mater Sci Lett, 2001, 20: 1741-743 14. Park K, Seong J K, Nahm S. J Alloys Compd, 2008, 455: 331-35 CrossRef 15. Noh W, Shin Y, Kim J, et al. Solid State Ionics, 2002, 152-53: 827-32 CrossRef 16. Bhandari C M, Rowe D M. Optimization of Carrier Concentration. Boca Raton: CRC Press, 1995. 43-6 17. Gao Y W, He Y Z, Zhu L L. Chin Sci Bull, 2010, 55: 16-1 CrossRef
作者单位:Liang Dong (1) HanJun Chen (1) YingJie Gan (2) Yu Wang (1) Xiang Dong (1) ShuJie Peng (2)
1. School of Electrical Engineering, Southwest Jiaotong University, Chengdu, 610031, China 2. School of Material Science and Engineering, Southwest Jiaotong University, Chengdu, 610031, China
ISSN:1861-9541
文摘
Tungsten trioxide ceramics were prepared from nm-sized powder precursors. Thermoelectric properties of samples were investigated. The results demonstrated that ceramics prepared in this manner have improved electrical conductivity and Seebeck coefficient values. The power factor of these samples also improved markedly, the largest power factor being 0.027 μW m? K? at 773 K.