Preparation, Structure, and Electrical Properties of Ca1鈭?em class="a-plus-plus">x Er x MnO3 Powders

详细信息    查看全文

• 作者：Yunjiao Li (1)
  Sue Hao (1)
  Xue Xia (1)
  Jialin Xu (1)
  Xin Du (1)
  Siyu Fang (1)
  Xianwei Meng (1)
  
• 关键词：CaMnO3 ; rare earths ; Er ; doping ; electrical properties
• 刊名：Journal of Electronic Materials
• 出版年：2013
• 出版时间：April 2013
• 年：2013
• 卷：42
• 期：4
• 页码：745-751
• 全文大小：624KB
• 参考文献：1. Y. Wang, Y. Sui, X.J. Wang, W.H. Su, and X.Y. Liu, / J. Appl. Phys. 108, 063928 (2010). CrossRef
  2. B. Raveau, A. Maignan, C. Martin, and M. Hervieu, / Chem. Mater. 10, 2641 (1998). CrossRef
  3. F.P. Zhang, X. Zhang, Q.M. Lu, J.X. Zhang, Y.Q. Liu, R.F. Fan, and G.Z. Zhang, / Physica B 406, 1258 (2011). CrossRef
  4. T. Okuda and Y. Fujii, / J. Appl. Phys. 108, 103702 (2010). CrossRef
  5. Y. Murano, M. Matsukawa, S. Ohuchi, S. Kobayashi, S. Nimori, R. Suryanarayanan, K. Koyama, and N. Kobayashi, / Phys. Rev. B 83, 054437 (2011). CrossRef
  6. S.M. Choi, C.H. Lim, and W.S. Seo, / J. Electron. Mater. 40, 551 (2011). CrossRef
  7. F. Kawashima, X.Y. Huang, K. Hayashi, Y. Miyazaki, and T. Kajitani, / J. Electron. Mater. 38, 1159 (2009). CrossRef
  8. M. Ohtaki, H. Koga, T. Tokunaga, K. Eguchi, and H. Arai, / J. Solid State Chem. 120, 105 (1995). CrossRef
  9. Y. Tokura and N. Nagaosa, / Science 288, 462 (2000). CrossRef
  10. R. Vonhelmolt, J. Wecker, B. Holzapfel, L. Schultz, and K. Samwer, / Phys. Rev. Lett. 71, 2331 (1993). CrossRef
  11. R.M. Kusters, J. Singleton, D.A. Keen, R. Mcgreevy, and W. Hayes, / Physica B 155, 362 (1989). CrossRef
  12. S. Jin, T.H. Tiefel, M. McCormack, R.A. Fastnacht, R. Ramesh, and L.H. Chen, / Science 264, 413 (1994). CrossRef
  13. M.B. Salamon and M. Jaime, / Rev. Mod. Phys. 73, 583 (2001). CrossRef
  14. C.N.R. Rao, A.K. Cheetham, and R. Mahesh, / Chem. Mater. 8, 2421 (1996). CrossRef
  15. S. Lee, H.Y. Hwang, B.I. Shraiman, W.D. Rataliff, and S.W. Cheong, / Phys. Rev. Lett. 82, 4508 (1999). CrossRef
  16. E. Dagotto, / Science 309, 257 (2005). CrossRef
  17. L. Sudheendra, A.R. Raju, and C.N.R. Rao, / J. Phys. Condens. Mater. 15, 895 (2003). CrossRef
  18. C. Silveira, M.E. Lopes, M.R. Nunes, and M.E. Melo Jorge, / Solid State Ionics 180, 1702 (2010). CrossRef
  19. J.W. Park, D.H. Kwak, S.H. Yoon, and S.C. Choi, / J. Alloys Compd. 487, 550 (2009). CrossRef
  20. J.L. Lan, Y.H. Lin, A. Mei, C.W. Nan, Y. Liu, B.P. Zhang, and J.F. Li, / J. Mater. Sci. Technol. 25, 535 (2009).
  21. T. Yamashita, / Mater. Chem. Phys. 103, 461 (2007). CrossRef
  22. A. Shukla and R.N.P. Choudhary, / J. Mater. Sci. 47, 5074 (2012). CrossRef
  23. J. Spooren, R.I. Walton, and F. Millange, / J. Mater. Chem. 15, 1542 (2005). CrossRef
  24. S.A. Mirji, Y.B. Khollam, S.B. Deshpande, H.S. Potdar, R.N. Bathe, S.R. Sainkar, and S.K. Date, / Mater. Lett. 58, 837 (2004). CrossRef
  25. S. Ramanathan, P.K. Singh, M.B. Kakade, and P.K. De, / J. Mater. Sci. 39, 3207 (2004). CrossRef
  26. C.S. Sanmathi, Y. Takahashi, D. Sawaki, Y. Klein, R. Retoux, I. Terasaki, and J.G. Noudem, / Mater. Res. Bull. 45, 558 (2010). CrossRef
  27. P.H. Isasi, M.E. Lopes, M.R. Nunes, and M.E.M. Jorge, / J. Phys. Chem. Solids 70, 405 (2009). CrossRef
  28. C. Lucas, I. Eiroa, M.R. Nunes, P.A. Russo, M.M.L.R. Carrott, M.I.S. Pereira, and M.E.M. Jorge, / J. Solid State Electron. 13, 943 (2009). CrossRef
  29. D. Sousa, M.R. Nunes, C. Silveira, I. Matos, A.B. Lopes, and M.E.M. Jorge, / Mater. Chem. Phys. 109, 311 (2008). CrossRef
  30. S.T. Aruna, M. Muthuraman, and K.C. Patil, / J. Mater. Chem. 7, 2499 (1997). CrossRef
  31. K. Nakade, K. Hirota, M. Kato, and H. Taguchi, / Mater. Res. Bull. 42, 1069 (2007). CrossRef
  32. L. Simonot, F. Garin, and G. Maire, / Appl. Catal. B Environ. 11, 181 (1997). CrossRef
  
• 作者单位：Yunjiao Li (1)
  Sue Hao (1)
  Xue Xia (1)
  Jialin Xu (1)
  Xin Du (1)
  Siyu Fang (1)
  Xianwei Meng (1)
  
  1. Department of Chemistry, Harbin Institute of Technology, Harbin, 150001, China
  
• ISSN：1543-186X

文摘

To improve the electrical properties of modified CaMnO3 powders, we synthesized Ca1鈭?em class="a-plus-plus">x Er x MnO3 (CEM) (0聽鈮ぢ?em class="a-plus-plus">x聽鈮ぢ?.3) powders by sol鈥揼el autocombustion technology. The effects of the Er-doping concentration on the structure and electrical properties of the powders were studied. The results show that Er-doping can decrease the resistivity of the CEM powders effectively and the variation of the resistivity presents a typical V-type with increasing Er-doping concentration. The resistivity reaches the lowest point of 0.5258聽惟聽m at x聽=聽0.25. Meanwhile, the Ca0.75Er0.25MnO3 powder showed good frequency stability and higher conductivity at high temperatures. x-Ray diffraction (XRD) patterns and valence analysis illustrate that the grain size and average valence of the Mn ions, which relate to the resistivity of the CEM powders, are affected by the Er-doping concentration. When x聽=聽0.25, the average valence of the Mn ions reaches the lowest point of 3.576. Scanning electron microscopy (SEM) analysis demonstrates that higher Er-doping concentration leads to smaller grain size in the CEM powders. Er-doping restrains the growth of the powder particles while decreasing the porosity and increasing the unit cell volume, resulting in improvement of the electrical properties of the modified powders.