参考文献:1. Kosolapova, T.Ya., / Tugoplavkie nitridy (Refractory Nitrides), Kiev: Naukova Dumka, 1983. 2. Samsonov, G.V., / Nemetallicheskie nitridy (Nonmetallic Nitrides), Moscow: Metallurgiya, 1969. 3. Gorlanov, E.S., Borisoglebskii, Yu.V., Vetyukov, M.M., and Akhmedov, S.N., / Tsvetn. Met., 1992, no. 1, pp. 24-5. 4. Schwarzkopf, P. and Kieffer, R., / Refractory Hard Metals New York: Macmillan, 1953, p. 21. 5. Todd, J.B., / J. Metals, 1981, vol. 33, no. 9, pp. 42-5. 6. Thonstad J., Fellner P., Haarberg G.M. et al., / Aluminium Electrolysis. Fundamentals of the Hall-Heroult Process, Dusseldorf: Aluminium-Verlag, 2001. 7. Yang, J., Hryn, J.N., Davis, B.R., and Roy, A., / Light Metals, 2004, pp. 321-26. 8. Apisarov, A.P., Tkacheva, O.Yu., and Zaikov, Yu.P., / Rastvorimost-glinozema v nizkotemperaturnykh elektrolitakh na osnove kalievogo kriolita: Tezisy dokl. Chast-II (Solubility of Alumina in Low-Temperature Electrolytes Based on Potassium Cryolite: Abstracts of Reports. Part II), Novomoskovsk: Ross. Univ. Chem. Technol., Novomoskovsk Inst., 2006, pp. 3-. 9. Kryukovsky, V.A., Frolov, A.V., Tkatcheva, O.Yu. et al., / Light Metals, 2006, pp. 409-13. 10. Yang, J., Hryn, J.N., and Krumdick, G.K., / Light Metals, 2006, pp. 421-24. 11. Redkin, A., Tkatcheva, O., Zaikov, Y., and Apisarov, A., / Light Metals, 2007, pp. 513-18. 12. Chartrand, P. and Heyrman, M., / Light Metals, 2007, pp. 519-24. 13. Wang, J., Lai, Y., Tian, Z., et al., / Light Metals., 2007, pp. 525-30. 14. Kan, H., Wang, Z., Shi, Z., et al., / Light Metals., 2007, pp. 531-36. 15. Yang, J.-H., Graczyk, D.G., Wunsch, C., and Hryn, J., / Light Metals, 2007, pp. 537-44. 16. Chuikin, A.Yu., Beketov, D.A., Malkov, V.B. et al., in / Vestn. Ural Gos. Tekh. Univ.-Ural Politekh. Inst., Ser. Khim, Yekaterinburg: Ural Gos. Tekh. Univ.-Ural Politekh. Inst. (UGTU-UPI), 2005, pp. 82-6.
作者单位:A. Yu. Chuikin (1) Yu. P. Zaikov (1) A. R. Beketov (2)
1. Institute of High-Temperature Electrochemistry, Ural Branch, Russian Academy of Sciences, ul. Akademicheskaya 20, Yekaterinburg, 620990, Russia 2. Ural Federal University, ul. Mira 19, Yekaterinburg, 620002, Russia
ISSN:1934-970X
文摘
Interaction kinetics of the aluminum nitride-based sintered composite material with the potassium cryolite melt with the cryolite ratio KO = 1.3 at 700-00°C is investigated by the continuous weighing method. It is established that the composite is almost unaffected by the melt at t = 700°C. The corrosion rate increases as the temperature increases. The material interacts with the molten salt through its oxidation stage by oxygen dissolved in the melt. This is also accompanied by the dissolution of oxygen-containing impurities that are initially present in the material. No interaction of sintered aluminum nitride with the melt under study was observed in the absence of the oxidant and with the concentration of alumina dissolved in cryolite close to saturation.