Effect of Thixoforming on the Microstructure and Tensile Properties of A356 Alloy and A356-5TiB2 In-situ Composite
详细信息 查看全文
- 作者：S. Deepak Kumar ; A. Mandal…
- 关键词：Semi ; solid metal processing ; Thixoforming ; Cooling slope casting ; A356 alloy ; TiB2 ; In situ composites
- 刊名：Transactions of the Indian Institute of Metals
- 出版年：2015
- 出版时间：September 2015
- 年：2015
- 卷：68
- 期：2-supp
- 页码：123-130
- 全文大小：2,377 KB
- 参考文献：1.Flemings M C, Metall Trans A, 22A (1991) 957.CrossRef
2.Cho W G, and Kang C G, J Mater Process Technol 105 (2000) 269.CrossRef
3.Fan Z, Int Mater Rev 47 (2002) 37.CrossRef
4.Atkinson H V, Prog Mater Sci 50 (2005) 341.CrossRef
5.Haga T, and Suzuki S, J Mater Process Technol 118 (2001) 169.CrossRef
6.Haga T, and Kapranos P, J Mater Process Technol 130–131 (2002) 581.CrossRef
7.Das P, Samanta S K, Venkatpathi B R K, Chattopadhyay H, and Dutta P, Trans Indian Inst Met 65 (2012) 669.CrossRef
8.Birol Y, J Mater Process Technol 186 (2007) 94.CrossRef
9.Das P, Samanta S K, Chattopadhyay H, and Dutta P, Acta Metall Sin (Engl Lett) 25 (2012) 329.
10.Deepak Kumar S, Pandu Ranga V, Mantry S, Mandal A, and Chakraborty M, Proc Mater Sci 5 (2014) 232.CrossRef
11.Dodangeh A, Kazeminezhad M, and Aashuri H, Mater Sci Eng A 558 (2012) 371.CrossRef
12.Tahamtan S, Golozar M A, Karimzadeh F, and Niroumand B, Mater Charact 59 (2008) 223.CrossRef
13.Fadavi Boostani A, and Tahamtan S, Mater Des 31 (2010) 3769.CrossRef
14.Mandal A, Chakraborty M, and Murty B S, Mater Sci Eng A 489 (2008) 220.CrossRef
15.Harsha Nandam S, Sankaran S, and Murty B S, Trans Indian Inst Met 64 (2011) 123.CrossRef
16.Kumar S, Chakraborty M, Subramanya Sarma V, and Murty B S, Wear 265 (2008) 134.CrossRef - 作者单位：S. Deepak Kumar (1)
A. Mandal (2)
M. Chakraborty (3)
1. School of Mechanical Sciences, Indian Institute of Technology Bhubaneswar, Bhubaneswar, 751007, Odisha, India
2. School of Minerals, Metallurgical and Materials Engineering, Indian Institute of Technology Bhubaneswar, Bhubaneswar, 751007, Odisha, India
3. Department of Metallurgical and Materials Engineering, Indian Institute of Technology Kharagpur, Kharagpur, 721302, West Bengal, India - 刊物类别：Chemistry and Materials Science
- 刊物主题：Materials Science
Metallic Materials
Materials Science, general
Tribology, Corrosion and Coatings - 出版者：Springer India
- ISSN：0975-1645
文摘
In the present work, A356 alloy and in situ A356-5TiB2 composite feedstock was produced by employing Cooling slope casting technique. The technique resulted in near spherical morphology of primary α-Al phase in the feedstock of both the alloy and composite. A fine distribution of eutectic Si phase within the matrix was observed in the composite feedstock. The rheocast billets of both the alloy and composite were then thixoformed successfully at 50 % solid fraction temperatures of 580 and 585 °C respectively. Further, tensile properties of thixoformed alloy and composite were measured and compared with those of gravity-cast samples. It was observed that the % increase in yield strength and tensile strength of thixoformed alloy increased by 43 and 36 % respectively with respect to the gravity-cast alloy. The thixoformed composite attained the highest ultimate tensile strength of 211 MPa which is about 40 % higher as compared to gravity-cast alloy. Interestingly, the ductility of the composites is comparable to that of alloy after thixoforming.