文摘
In this study, the Ni–Al2O3 nanocomposite multilayer coatings with six consecutive layers were electrodeposited on the mild steel by pulse electrodeposition with ultrasound agitation from nickel Watts-type bath. The structure and morphology of the etched coatings cross-section were characterized by scanning electron microscopy (SEM). The corrosion behaviour of these coatings was investigated in 1 M H2SO4 solution. All of the coatings showed the active–passive transition and the distinct difference in structure had negative influence on their corrosion resistance. Moreover, the tribological behaviour of these coatings was evaluated by pin-on-disc type. The results showed that wear resistance increased with increase in duty cycle and frequency.