Production of core-sheath nanofiber yarn using two opposite asymmetric nozzles

详细信息    查看全文

• 作者：Aref Fakhrali ; Seyed Vahid Ebadi ; Ali Aakbar Gharehaghaji
• 关键词：Electrospinning ; Nanofiber ; Hollow nanofiber yarn ; Core ; sheath nanofiber yarn ; Mechanical properties
• 刊名：Fibers and Polymers
• 出版年：2014
• 出版时间：December 2014
• 年：2014
• 卷：15
• 期：12
• 页码：2535-2540
• 全文大小：712 KB
• 参考文献：1. D. Li and Y. N. Xia, / Adv. Mater., 16, 1151 (2004). CrossRef
  2. D. H. Reneker and I. Chun, / Nanotechnology, 7, 216 (1996). CrossRef
  3. M. Abbasipour and R. Khajavi, / Adv. Polym. Tech., 32, 21363 (2013). CrossRef
  4. F. L. Zhou and R. H. Gong, / Polym. Int., 57, 837 (2008). CrossRef
  5. P. D. Dalton, D. Klee, and M. M?ller, / Polym. Int., 46, 611 (2005). CrossRef
  6. S. F. Fennessey and R. J. Farris, / Polym. Int., 45, 4217 (2004). CrossRef
  7. M. Hamedi, R. Forchheimer, and O. Ingan?s, / Nat. Mater., 6, 357 (2007). CrossRef
  8. M. S. Khil, S. R. Bhattarai, H. Y. Kim, S. Z. Kim, and K. H. Lee, / J. Biomed. Mater. Res., 72, 117 (2005). CrossRef
  9. H. Y. Kim, M. S. Gil, Y. H. Jung, H. J. Kim, and B. S. Lee, / U.S. Patent, 10512095 (2005).
  10. A. Formhals, / U.S. Patent, 1975504 (1934).
  11. A. Formhals, / U.S. Patent, 2123992 (1938).
  12. A. Formhals, / U.S. Patent, 2109333 (1938).
  13. A. Formhals, / U.S. Patent, 2160962 (1939).
  14. A. Formhals, / U.S. Patent, 2187306 (1940).
  15. A. Formhals, / U.S. Patent, 2323025 (1943).
  16. A. Formhals, / U.S. Patent, 2349950 (1944).
  17. H. Fong, W. Liu, C. S. Wang, and R. A. Vaia, / Polymer, 43, 775 (2001). CrossRef
  18. H. Okuzaki, T. Takahashi, Y. Hara, and H. Yan, / J. Polym. Sci. Pol. Phys., 46, 305 (2008). CrossRef
  19. H. Okuzaki, T. Takahashi, N. Miyajima, Y. Suzuki, and T. Kuwabara, / Macromolecules, 39, 4276 (2006). CrossRef
  20. X. Wang, K. Zhang, M. Zhu, B. S. Hsiao, and B. Chu, / Macromol. Rapid. Comm., 29, 826 (2008). CrossRef
  21. X. Wang, K. Zhang, M. Zhu, H. Yu, Z. Zhou, Y. Chen, and B. S. Hsiao, / Polymer, 49, 2755 (2008). CrossRef
  22. E. Smit, U. Buttner, and R. D. Sanderson, / Polymer, 46, 2419 (2005). CrossRef
  23. W. E. Teo, R. Gopal, R. Ramaseshan, K. Fujihara, and S. Ramakrishna, / Polymer, 48, 3400 (2007). CrossRef
  24. M. Yousefzadeh, M. Latifi, W. E. Teo, M. Amani-Tehran, and S. Ramakrishna, / Polym. Eng. Sci., 51, 323 (2010). CrossRef
  25. A. F. Lotus, E. T. Bender, E. A. Evans, R. D. Ramsier, D. H. Reneker, and G. G. Chase, / J. Appl. Polym. Sci., 103 (2008).
  26. W. Teo and S. Ramakrishna, / Nanotechnology, 17, 89 (2006). CrossRef
  27. N. Li, Q. Hui, H. Xue, and J. Xiong, / M
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Chemistry
  Polymer Sciences
  
• 出版者：The Korean Fiber Society
• ISSN：1875-0052

文摘

In this study, a new design of electrospinning is presented to produce core-sheath and hollow nanofiber yarns. Sample core-sheath nanofiber yarns were produced from PVA nanofibers as core and PA6 nanofibers as sheath. PVA portion was extracted by treating in boiled water from the core of yarn structure and a PA6 hollow nanofiber yarn was resulted. The surface structure was studied by scanning electron microscopy (SEM). Also the mechanical properties of these yarns were investigated. The results showed that the PA6 nanofiber diameter in core-sheath and hollow nanofiber yarn was ranging from 92±20 and 109±23 nm, respectively. SEM images confirmed the core-sheath and hollow structure of these nanofiber yarns clearly. Examination of the strength of the core-sheath and hollow nanofiber yarn by tensile tester was carried out and resulted in 59.60±9.32 and 83.90±16.88 MPa respectively. These yarns have potential applications in various fields such as tissue engineering and drug delivery.