High formability of glass plus fcc-Al phases in rapidly solidified Al-based multicomponent alloy

详细信息    查看全文

• 作者：F. F. Han ; A. Inoue ; Y. Han ; F. L. Kong ; S. L. Zhu…
• 刊名：Journal of Materials Science
• 出版年：2017
• 出版时间：February 2017
• 年：2017
• 卷：52
• 期：3
• 页码：1246-1254
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Materials Science, general; Characterization and Evaluation of Materials; Polymer Sciences; Continuum Mechanics and Mechanics of Materials; Crystallography and Scattering Methods; Classical Mechanics;
• 出版者：Springer US
• ISSN：1573-4803
• 卷排序：52

文摘

A multicomponent Al₈₄Y₉Ni₄Co_1.5Fe_0.5Pd₁ alloy was found to keep a mixed glassy + Al phases in the relatively large ribbon thickness range up to about 200 μm for the melt-spun ribbon and in the diameter range up to about 1100 μm for the wedge-shaped cone rod prepared by injection copper mold casting. The glassy phase in the Al-based alloy has a unique crystallization process of glass transition, followed by supercooled liquid region, fcc-Al + glass, and then Al + Al₃Y + Al₉ (Co, Fe)₂ + unknown phase. It is also noticed that the primary precipitation phase from supercooled liquid is composed of an Al phase instead of coexistent Al + compound phases, being different from the crystallization mode from supercooled liquid for ordinary Al-based glassy alloys. In addition, it is noticed that the mixed Al and glassy phases are extended in a wide heating temperature range of 588–703 K, which is favorable for the development of high-strength nanostructure Al-based bulk alloys obtained by warm extrusion of mixed Al + amorphous phases. The Vickers hardness is about 415 for the glassy phase and increases significantly to about 580 for the mixed Al and glassy phases. The knowledge of forming Al + glassy phases with high hardness in the wide solidification and annealing conditions through high stability up to complete crystallization for the multicomponent alloy is promising for future development of a high-strength Al-based bulk alloy.