文摘
The microstructure and mechanical properties of laser-welded high-strength Mg-Gd-Y-Zr alloy in T6 condition were investigated. The network-distributed precipitates at grain boundaries were identified as the Mg24(Gd,Y)5. No significant grain coarsening was observed in the heat-affected zone. The deterioration of mechanical properties was attributed to the dissolution of precipitates in the heat-affected zone during laser welding. For the weakest part of the heat-affected zone, solid solution strengthening was the most important strengthening factor.