文摘
This work presents results observed after the first 5 h of oxidation of Haynes® 282® alloy. The steam oxidation tests have been carried out in pure water at 760 °C for 1, 2 and 5 h, respectively, using an accurate thermogravimetric balance technique. The alloy used for comparison in this work was fabricated using three different methods. The initial steam oxidation performance of the commercially wrought alloy Haynes® 282® was compared with a fabricated cast alloy and a HIP/PM alloy. The results show that in terms of corrosion resistance, fabrication techniques appear to have little impact on steam oxidation performance and behavior. The exposed Ni-based alloys all developed the oxide scales consisting mainly of Cr2O3 phase mixed with some TiO2, while internal Al and Ti precipitations along the grain boundaries were observed both in Haynes® 282® wrought and HIP/PM alloy.