摘要
Li-rich Mn-based Lib>1+xb>(Mnb>0.533b>Nib>0.233b>Cob>0.233b>)b>1鈭?em>xb>Ob>2b> (x = 0, 0.045, 0.09, 0.135, 0.18, 0.225) materials have been prepared by a conventional solid-state reaction. XRD, SEM and half-cell tests are investigated on the influence of Li content. Pure phase can be obtained when Li-excessive value x keeps between 0.045 and 0.18. The initial efficiency (Qb>1db>/Qb>1cb>) almost keeps the same level of 70%for different Li-excessive samples. Lib>1.045b>Mnb>0.509b>Nib>0.223b>Cob>0.223b>Ob>2b> sample shows highest discharge capacity of 259.8 mA h g鈭?. Lib>1.09b>Mnb>0.486b>Nib>0.212b>Cob>0.212b>Ob>2b> sample exhibits the best rate capability, and almost no reduction is observed after 24-time cycles in different discharge current density.