Nanocrystallization in Fe₈₁B_13.5Si_3.5C₂ amorphous magnetic ribbons

详细信息	查看全文 | 推荐本文 |

• 作者：W. Pon-On ; P. Winotai
• 关键词：Nanocrystallization ; Fe₈₁B_13.5Si_3.5C₂ ribbon ; Hysteresis ; Mö ; ssbauer
• 刊名：Journal of Magnetism and Magnetic Materials
• 出版年：2008
• 期刊代码：31_03048853
• 类别：ph
• 出版时间：February 2008
• 卷：320
• 期：3-4
• 页码：81-90
• 文件大小：885 K

摘要

Nanocrystallization in amorphous ribbons Fe₈₁B_13.5Si_3.5C₂ was fully investigated by using X-ray diffractometer (XRD), Mössbauer spectroscopy (MS), differential scanning calorimeter (DSC), and vibrating sample magnetometer (VSM) after annealing in the temperature range 400–600 °C for 2 h under argon atmosphere. DSC results show two exothermic peaks at 495 and 525 °C which clearly represent two crystallization temperatures corresponding to activation energies of 385 and 366 kJ/mol, respectively. Heat treatments of the ribbon below the first crystallization temperature yielded nanograins of the soft magnetic phase of α-Fe(Si) embedded in the remaining amorphous matrix. Mössbauer parameters originating from nanocrystalline phases of α-Fe(Si), t-Fe₂B, and t-Fe₃B (t for tetragonal), could be evaluated after annealing at 500 °C for 2 h. The presence of nanocrystalline phases was also confirmed by XRD patterns. The amorphous ribbon completely crystallizes into α-Fe, α-Fe(Si), t-Fe₂B, t-Fe₃B, and Fe₃C (orthorhombic) after 600 °C. The coercivity rapidly increases with the annealing temperature with the exception of the ribbon annealed at 425 °C which yields only the soft α-Fe(Si) nanocrystalline phase. The coercivity of ribbon increases to 6.25 and 10.56 Oe after 2-h annealing at 425 and 475 °C, respectively, compared to that of as-cast sample, 5.29 Oe. However, it increases sharply to 61.11 and 74.99 Oe after heat treatments at 525 and 575 °C, respectively. Meanwhile, M_r increases sharply from as-cast value 3.26 to 43.64 emu/g after 2-h annealing at 575 °C. However, M_s shows only slight increase from the as-cast value of 165.53 to 207.99 emu/g after 2 h annealing at 575 °C.