摘要
The electrodeposition of cobalt-antimony thermoelectric semiconductor films was investigated in a non-aqueous solution of ethylene glycol (EG)-CoCl2-SbCl3 at 393 K. By controlling the bath composition and cathodic current density, Co-Sb alloys containing 0-94 mol%of Co were obtained at 50-300 Am鈭?#xA0;2. The resistance polarization caused by the formation of semiconductor film was observed in the polarization curve measured in the EG-CoCl2-SbCl3 (90.0-9.3-0.7 mol%) bath. In this bath, the Co-Sb (23.6-76.4 mol%) alloy was obtained by maintaining the constant potential electrolysis at 0.1 V. This alloy included CoSb3 and exhibited a p-type thermoelectric conversion by the given temperature difference.