The electrical conductivity and oxygen permeation of ceria with alumina addition at high temperature

详细信息	查看全文 | 推荐本文 |

• 作者：Hee Jung Park ; Gyeong Man Choi
• 关键词：Electrical conductivity ; Oxygen permeation ; Ceria ; Alumina ; Mechanical stability
• 刊名：Solid State Ionics
• 出版年：2008
• 期刊代码：96_01672738
• 类别：ch
• 出版时间：31 January 2008
• 卷：178
• 期：33-34
• 页码：1746-1755
• 文件大小：1265 K

摘要

Acceptor-doped ceria can be used as an oxygen-permeating membrane due to its high mixed ionic and electronic conductivity at high temperature in low oxygen partial pressure. However, the mechanical weakness prevented its use at a high temperature in the reducing condition. In this study, alumina was added to strengthen the ceria without severely reducing the electrical conductivity. The electrical conductivity of alumina-added ceria, (Ce_0.8Gd_0.2O_{2 − δ})_{1 − x} + (Al₂O₃)_x (x = 0, 0.019, 0.0475, and 0.095: hereafter, GDC20, GDCA2, GDCA5, GDCA10, respectively), was measured as a function of temperature (1300 °C–1600 °C) and oxygen partial pressure (P_O2: 1–10^{− 13} atm). As the alumina content increased, the ionic conductivity decreased due to the formation of a secondary phase (~ Gd_0.8Ce_0.2AlO₃) which caused a decrease in the Gd content in the ceria. The conductivities of GDC20 with and without alumina addition showed maxima in the conductivity curves in the reducing condition when plotted versus log P_O2. The oxygen-permeation values of GDC20, GDCA5, and GDCA10, measured at 1500 and 1600 °C in the high P_O2 range (0.21–0.02 atm), were much higher than that of doped-zirconia. The permeation rate slightly decreased with the alumina addition. The oxygen permeation of the ceria-based sample, GDCA10, in the low P_O2 range (2 × 10^{− 10}–2 × 10^{− 8} atm) was successfully measured at 1600 °C for the first time and showed much higher (> 50 times) oxygen permeability than that of the doped-zirconia.