A series of manganese-ceria supported on alumina catalysts with various Mn/Ce ratios are investigated in both methanol decomposition to CO and hydrogen and SCR of NOx with CO. The study is aimed at the potential application of both reactions in integrated devices, where NOx is reduced with the products of the decomposed methanol. The samples are characterized by nitrogen physisorption, XRD, TEM, XPS, UV-Vis, and TPR. It was established that manganese-ceria supported on alumina catalysts are perspective in both methanol decomposition and NO reduction at temperatures above 723 K, which are typical for exhausted gases from the vehicles and some stationary stations. The best catalytic activity and selectivity to the desired products under these conditions was found for the samples with Mn/Mn + Ce ratio of 0.5 and 0.7. This superior catalytic performance is related to the formation of mixed valence Mn3+/Ce4+ and Mn4+/Ce3+ active sites.