Mechanisms of dynamic deformation and dynamic failure in aluminum nitride

详细信息	查看全文 | 推荐本文 |

• 作者：Guangli Hu^a ; C.Q. Chen^a ; K.T. Ramesh^a ; ^{ramesh@jhu.edu} ; J.W. McCauley^b
• 关键词：Sintering ; Fracture ; Deformation ; Micromechanical modeling ; Dislocations
• 刊名：Acta Materialia
• 出版年：2012
• 期刊代码：1_13596454
• 类别：ms
• 出版时间：May, 2012
• 卷：60
• 期：8
• 页码：3480-3490
• 文件大小：1348 K

摘要

Uniaxial quasi-static, uniaxial dynamic and confined dynamic compression experiments have been performed to characterize the failure and deformation mechanisms of a sintered polycrystalline aluminum nitride using a servohydraulic machine and a modified Kolsky bar. Scanning electron microscopy and transmission electron microscopy (TEM) are used to identify the fracture and deformation mechanisms under high rate and high pressure loading conditions. These results show that the fracture mechanisms are strong functions of confining stress and strain rate, with transgranular fracture becoming more common at high strain rates. Dynamic fracture mechanics and micromechanical models are used to analyze the observed fracture mechanisms. TEM characterization of fragments from the confined dynamic experiments shows that at higher pressures dislocation motion becomes a common dominant deformation mechanism in AlN. Prismatic slip is dominant, and pronounced microcrack-dislocation interactions are observed, suggesting that the dislocation plasticity affects the macroscopic fracture behavior in this material under high confining stresses.