Microstructure evolution and tribological properties of TiB₂/Ni-Ta cermets

详细信息	查看全文 | 推荐本文 |

• 作者：Ľ ; uboš ; Bač ; a^a ; ; Zoltá ; n Lenč ; é ; š ; ^b ; Christian Jogl^a ; Erich Neubauer^c ; Martin Vitkovič ; ^b ; Andreas Merstallinger^a ; Pavol Š ; ajgalí ; k^b
• 关键词：Hot-pressing ; Microstructure-final ; Wear resistance ; Borides ; Wear parts
• 刊名：Journal of the European Ceramic Society
• 出版年：2012
• 期刊代码：53_09552219
• 类别：ms
• 出版时间：July, 2012
• 卷：32
• 期：9
• 页码：1941-1948
• 文件大小：2290 K

摘要

Cermets containing TiB₂ and single or mixed metals were produced by conventional hot-pressing technique at 2100 掳C for 1 h. Nickel, tantalum and their mixtures were used as alloying substances to enhance the density of TiB₂ composites. The influence of metal addition on the microstructure and tribological properties were investigated. The addition of Ta powder greatly refined the microstructure of sintered samples. Similarly, the mixture of Ni and Ta metals hindered the grain growth of TiB₂ particles during the hot-pressing while the samples were sintered up to 98%of theoretical density. The wear behaviour of the composites was assessed by ball on disk tests. The wear rate against alumina counterbody varied in the range of (5.9-21.2) 脳 10^鈭? mm³/Nm. The friction coefficient was not affected significantly by the alloying substances and only slightly increased from 0.58 for pure TiB₂ to 0.67 for samples with Ta addition.