Preparation of zeolite-coated cordierite honeycombs prepared by an in situ crystallization method

详细信息	查看全文 | 推荐本文 |

• 作者：Okada ; Kiyoshi ; Kameshima ; Yoshikazu ; Madhusoodana ; Chengala D. ; Das ; Rathindra N.
• 关键词：Zeolite films ; In situ crystallization ; Porous properties ; Microstructure ; Hydrothermal treatment
• 刊名：Science and Technology of Advanced Materials
• 出版年：2004
• 期刊代码：156_14686996
• 类别：et
• 出版时间：July, 2004
• 卷：5
• 期：4
• 页码：479-484
• 文件大小：360 K

摘要

Zeolite thin films were prepared on cordierite (Mg₂Al₄Si₅O₁₈) honeycomb substrates by in situ crystallization using soft hydrothermal conditions. The synthesized zeolite films (zeolite A and ZSM-5) were characterized by XRD, FTIR, SEM, NH₃-TPD, and Ns₂ and propane gas adsorption. Zeolite-A films were prepared by dip-coating on a cordierite substrate in a precursor of molar composition of Na₂O:Al₂O_3: SiO_2: H₂O=4:1:2:100 and heating in an autoclave at 80 °C for 6–10 h. The resultant zeolite-A films consisted of cubic crystals about 2–3 μm in size, achieving a thickness of 20 μm after re-coating. ZSM-5 films were similarly formed using a microporous silica precursor obtained by selective leaching of metakaolinite with tetrapropylammonium hydroxide (TPAOH) as the templating agent. The molar composition of the precursor was NaOH:microporous silica:TPAOH:H₂O=1:10:1:200. The dipped substrate covered with the wet precursor gel was heated in an autoclave at 150 °C for 24 h. The resultant films were composed of short prismatic <1 μm crystals achieving thickness of several to 10 μm after re-coating. The microstructure and porous properties of the ZSM-5 films were found to change according to the chemical composition and surface treatment of the cordierite substrates. The presence of a SiO₂-rich interfacial layer between the substrate and zeolite film increased the amount of zeolite formed and the physical adsorption but decreased the solid acidity and amount of chemisorption.