Copper doped lanthanum strontium ferrite showed superior kinetics for the electro-reduction of oxygen. The generic formulation was La1芒芒芒xSrxCu1芒芒芒yFeyO3 (LSCuF) where x ranged from 0.2 to 0.3 and y varied from 0 to 0.4. Doping with copper improved the electrocatalytic activity compared with undoped material. In oxygen, the La0.7Sr0.3Cu0.2Fe0.8O3 sample showed current densities approximately 2芒芒芒3 times that of La0.7Sr0.3FeO3 and 10 times that of La0.8Sr0.2FeO3. This improvement was confirmed with cyclic voltammetric studies on half cells and on full fuel cell tests. Copper doped materials have unusual electrochemical characteristics and copper apparently undergoes a one electron reduction at overpotentials less than 芒芒芒0.1 V. This occurred only in air but not in oxygen.