Single crystal growth from the melt and magnetic properties of hexaferrites-aluminates

详细信息	查看全文 | 推荐本文 |

• 作者：S.G. Pavlova ; A.M. Balbashov ; ^{balbashovAM@mpei.ru} ; L.N. Rybina
• 关键词：A2. Crystal growth ; A2. Floating zone ; Bl. Hexaferrites ; B1. Oxide materials ; B3. Gas pressure.
• 刊名：Journal of Crystal Growth
• 出版年：2012
• 期刊代码：49_00220248
• 类别：ch
• 出版时间：15 July, 2012
• 卷：351
• 期：1
• 页码：161-164
• 文件大小：371 K

摘要

Single crystals of aluminum substituted barium hexaferrite were grown by the floating zone method with optical heating. Single crystals were produced from a melt of stoichiometric composition. The process was carried out under a pressure of 50 atm of oxygen. In the system BaO-(x)Al₂O₃-(6鈭?em>x)Fe₂O₃ the region of single phase crystal growth from the melt is limited by the value x=3. For higher substitutions single-phase crystallization is not observed. The grown single crystals are cylindrical boules with a diameter of 4-5 mm and with lengths up to 50 mm. To avert cracking the crystals have been annealed during the process of growth at 1100 掳C. The content of FeO in the composition of single crystals of barium hexaferrite, grown by zone melting under an oxygen pressure of 50 atm, is approximately 0.3 wt%. In the system of hexaferrite-aluminates the macroscopic magnetic moment of the material disappears at x=3.